A light-colored rubber composition for fork-cutting tire includes 120-140 weight parts of standard rubber, 120-140 weight parts of cigarette film, 10-20 weight parts of zinc oxide, 4-10 weight parts of stearic acid, 100-150 weight parts of silica, 10-15 weight parts of silane coupling agent, 3-5 weight parts of sulphur, 6-12 weight parts of accelerator, 8-15 weight parts of reinforcing agent, 5-10 weight parts of antioxidant, and white oil. 15-20 parts by weight, 4-6 parts by weight of titanium dioxide and 0.3-0.5 parts by weight of carbon black. The combination of the above components has the advantages of high strength and hardness, good toughness, light color system, long-term use and non-discoloration.
【技术实现步骤摘要】
一种用于剪叉轮胎的浅色橡胶组合物
本专利技术涉及轮胎
，具体涉及一种用于剪叉轮胎的浅色橡胶组合物。
技术介绍
常见的轮胎通常为黑色，外观单一，难以满足多样化的装饰需求。为获得其他颜色的轮胎，需要使用浅色胶料，而现有的浅色胶料通常需要添加较多的浅色填料，如钛白粉进行调色，降低了轮胎的力学性能和使用寿命。此外，浅色胶料对防老剂要求较高，而黑色轮胎中常用的胺类防老剂等一系列高稳定性的防老剂在使用一段时间后易变色；其他的防老剂单独使用时往往抗老化作用较弱，难以保证浅色胎的色泽稳定性。因此，尚且缺乏一种力学性能好、使用寿命长且不易变色的浅色系轮胎用橡胶组合物。
技术实现思路
针对现有技术的上述问题，本专利技术提供一种用于剪叉轮胎的浅色橡胶组合物，具有较好的强度和韧性、较佳的硬度及较高的色泽稳定性，长期使用不易变色。为实现上述目的，本专利技术采用以下技术方案：一种用于剪叉轮胎的浅色橡胶组合物，包括以下组分：标准胶120～140重量份，烟片胶120～140重量份，氧化锌10～20重量份，硬脂酸4～10重量份，白炭黑100～150重量份，硅烷偶联剂10～15重量份，硫磺3～5重...
【技术保护点】
1.一种用于剪叉轮胎的浅色橡胶组合物，其特征在于，包括以下组分：标准胶120～140重量份，烟片胶120～140重量份，氧化锌10～20重量份，硬脂酸4～10重量份，白炭黑100～150重量份，硅烷偶联剂10～15重量份，硫磺3～5重量份，促进剂6～12重量份，补强剂8～15重量份，防老剂5～10重量份，白油15～20重量份，钛白粉4～6重量份，炭黑0.3～0.5重量份。
【技术特征摘要】
1.一种用于剪叉轮胎的浅色橡胶组合物，其特征在于，包括以下组分：标准胶120～140重量份，烟片胶120～140重量份，氧化锌10～20重量份，硬脂酸4～10重量份，白炭黑100～150重量份，硅烷偶联剂10～15重量份，硫磺3～5重量份，促进剂6～12重量份，补强剂8～15重量份，防老剂5～10重量份，白油15～20重量份，钛白粉4～6重量份，炭黑0.3～0.5重量份。2.根据权利要求1所述的用于剪叉轮胎的浅色橡胶组合物，其特征在于，所述标准胶和烟片胶的重量比为1:1。3.根据权利要求1或2所述的用于剪叉轮胎的浅色橡胶组合物，其特征在于，所述烟片胶为...
【专利技术属性】
技术研发人员：陈孟宏，
申请(专利权)人：长沙中京机械有限公司，
类型：发明
国别省市：湖南,43