The invention discloses an oil resistant and low temperature resistant rubber and a preparation method thereof. The rubber consists of the following weight components: natural rubber 50 80 phr, nitrile butadiene rubber 20 50 phr, carbon black 40 80 phr, plasticizer 5 20 phr, zinc oxide 2 20 phr, stearic acid 1 5 phr, antioxidant 1 10 phr, sulfur 1 8 phr, vulcanization accelerator 1 8 phr, processing aids 1 4 phr. Compared with ordinary rubber, the rubber of the invention has outstanding oil resistance and low temperature resistance, and has good physical and mechanical properties. The rubber of the invention has simple production method, low cost, good technological properties of rubber compound and is easy to industrialize production.
【技术实现步骤摘要】
一种耐油耐低温橡胶及其制备方法
本专利技术属于橡胶材料领域，特别是涉及一种耐油耐低温橡胶及其制备方法。技术背景随着橡胶材料在采掘、交通、建筑、机械、电子等重工业和新兴产业中的广泛应用，对橡胶材料的性能提出了更高的要求，特别是橡胶的耐油耐低温性能，而耐低温与耐油性能是一对矛盾体，根据相似相容原理，橡胶分子极性越强，小分子油品对其的渗透性越差，耐油性越好，而分子极性越强使分子间的相互作用越大，对分子链及链段的运动的束缚力也就越大，使得玻璃化转变温度Tg升高，从而使橡胶在一定低温下保持弹性的能力减弱，即耐低温性能变差。因此单一的橡胶基体材料已经不能满足使用需求。橡胶制品的性能除了和橡胶基体本身的性质有关，还与配合体系有密切联系，橡胶的耐寒性主要体现在分子链的运动能力较强，分子间的运动相对容易，分子凝聚的能量相对的低。当前最常用的解决办法之一是增塑剂的选择和使用，增塑剂能使橡胶分子运动变得容易，降低橡胶分子间的作用力，从而降低橡胶的玻璃化温度，改善橡胶可塑性和流动性，便于压延、压出等成型操作，同时还能改善硫化胶的某些物理机械性能，如降低硬度和定伸应力、赋予较高的弹性和...
【技术保护点】
1.一种耐油耐低温橡胶，其特征在于：所述的耐油耐低温橡胶由以下重量组份的原料组成：天然橡胶50‑80份、丁腈橡胶20‑50份、炭黑40‑80份、增塑剂5‑20份、氧化锌2‑20份、硬脂酸1‑5份、防老剂1‑10份、硫磺1‑8份、硫化促进剂1‑8份、加工助剂L‑181‑4份。
【技术特征摘要】
1.一种耐油耐低温橡胶，其特征在于：所述的耐油耐低温橡胶由以下重量组份的原料组成：天然橡胶50-80份、丁腈橡胶20-50份、炭黑40-80份、增塑剂5-20份、氧化锌2-20份、硬脂酸1-5份、防老剂1-10份、硫磺1-8份、硫化促进剂1-8份、加工助剂L-181-4份。2.根据权利要求1所述的一种耐油耐低温橡胶，其特征在于：所述的天然橡胶为颗粒胶、烟片胶、风干片胶、绉片胶中的任一种。3.根据权利要求1所述的一种耐油耐低温橡胶，其特征在于：所述的丁腈橡胶为丁腈橡胶1052，其中丙烯腈含量为31％-35％。4.根据权利要求1所述的一种耐油耐低温橡胶，其特征在于：所述的炭黑为高耐磨炭黑N330、通用炉黑N660、喷雾炭黑、半补强碳黑N774中的一种或几种组合。5.根据权利要求1所述的一种耐油耐低温橡胶，其特征在于：所述的增塑剂为聚醚类增塑剂TP-90B和醚酯型增塑剂TP-95中的一种。6.根据权利要求1所述的一种耐油耐低温橡胶，其特征在于：所述的防老剂为防老剂RD和防老剂BL...
【专利技术属性】
技术研发人员：简建，
申请(专利权)人：大连铁达塑胶制品有限公司，
类型：发明
国别省市：辽宁,21