The invention relates to the field of stainless steel manufacturing technology, in particular to a non-magnetic high corrosion-resistant nickel-saving austenitic stainless steel, which has the following components of mass percentage: C:0.06_0.13%, Si:0.2_0.6%, Mn:7.5_12.0%, Cr:18.0_20%, Ni:1.0_4.0%, Cu:1.5_3.5%, P<0.045%, S<0.0050%, N:0.18_30%, Mo:<1.0%, Nb<0.2%, Nb<0.0.0%. 0%, V < 0.20%, Ti < 0.20%, B < 0.0050%, Ca < 0.0050%, and Fe. The beneficial effect of the invention is that the non-magnetic high corrosion-resistant nickel-saving austenitic stainless steel of the invention not only has low cost, but also has high corrosion resistance as well as non-magnetic finished products and cold-processed products.
【技术实现步骤摘要】
一种无磁高耐蚀节镍奥氏体不锈钢
本专利技术涉及不锈钢制造
，具体涉及一种无磁高耐蚀节镍奥氏体不锈钢。
技术介绍
不锈钢根据金相组织可分为奥氏体、铁素体、马氏体以及双相钢等组织。其中铁素体、马氏体以及双相钢均是带磁性的组织。唯有奥氏体不锈钢是无磁的。随着科技发展日新月异，信息化、智能化是未来发展的一大趋势，对不锈钢产品无磁要求越来越高，在无磁的环境下进行智能信息传输越来越普遍。现有的S30400(典型的奥氏体不锈钢牌号为06Cr19Ni10，即304)不锈钢产品由于不可避免的冶炼成分偏析、热加工和热处理等各种原因，会造成304奥氏体不锈钢中产生少量铁素体或马氏体组织，使得304不锈钢中带有少量的磁性，而这些少量磁性干扰数据传输，造成智能数据传输错误或者中断，已经无法满足高标准产品性能需要。
技术实现思路
本专利技术解决的技术问题为：通过适当的合金元素设计，提供一种成本经济、耐蚀性高、磁性能良好的无磁高耐蚀节镍奥氏体不锈钢。为了实现上述目的，本专利技术采用的技术方案为提供一种无磁高耐蚀节镍奥氏体不锈钢，具有如下的质量百分比的组分：C：0.06-0.13％，Si：0....
【技术保护点】
1.一种无磁高耐蚀节镍奥氏体不锈钢，其特征在于，具有如下的质量百分比的组分：C：0.06‑0.13％，Cr：18.0‑20％，Si：0.2‑0.6％，Mn：7.5‑12.0％，S≤0.0050％，P≤0.045％，Ni：1.0‑4.0％，Cu：1.5‑3.5％，N：0.18‑0.30％，Mo：≤1.0％，Nb≤0.20％，V≤0.20％，Ti≤0.20％，B≤0.0050％；Ca≤0.0050％，余量为Fe和不可避免的杂质元素。
【技术特征摘要】
1.一种无磁高耐蚀节镍奥氏体不锈钢，其特征在于，具有如下的质量百分比的组分：C：0.06-0.13％，Cr：18.0-20％，Si：0.2-0.6％，Mn：7.5-12.0％，S≤0.0050％，P≤0.045％，Ni：1.0-4.0％，Cu：1.5-3.5％，N：0.18-0.30％，Mo：≤1.0％，Nb≤0.20％，V≤0.20％，Ti≤0.20％，B≤0.0050％；Ca≤0.0050％，余量为Fe和不可避免的杂质元素。2.根据权利要求1所述的无磁高耐蚀节镍奥氏体不锈钢，其特征在于，具有如下的质量百分比的组分：C：0.079％，Cr：18.12％，Si：0.35％，Mn：9.7％，S：0.0022％，P：0.033％，Ni：3.02％，Cu：1.75％，N：0.245％，Fe余量和不可避免的杂质元素。3.根据权利要求1所述的无磁高耐蚀节镍奥氏体不锈钢，其特征在于，具有如下的质量百分...
【专利技术属性】
技术研发人员：姜海洪，周庆龙，江来珠，蒋一，邹文辉，
申请(专利权)人：福建青拓特钢技术研究有限公司，
类型：发明
国别省市：福建,35