The invention discloses a sinterable electrode coating material and a preparation method. The electrode coating material consists of 21-33 nano-copper powders, 10-15 manganese dioxide, 6-10 cobalt chloride, 8-13 nickel oxide, 2-5 rubidium oxide, 15-18 binders and 1-3 surfactants by weight. The electrode coating material has excellent electrical conductivity and sinterability. By adding rare earth elements, the sintering performance of the coating is effectively improved, and dark cracking is avoided. The preparation method adopts inert gas for final treatment, which improves the elasticity of the coating and the sinterability of the coating, improves the production efficiency of the electrode, thus indirectly reducing the cost.
【技术实现步骤摘要】
一种易烧结的电极镀层材料及其制备方法
本专利技术属于电极材料领域，具体涉及一种易烧结的电极镀层材料及其制备方法。
技术介绍
电极镀层是在电极表面附着一层金属膜的工艺，起到防止金属氧化(如锈蚀)，提高耐磨性、导电性、反光性、抗腐蚀性(硫酸铜等)及增进美观等作用。电极镀层若按镀层的成分则可分为单一金属镀层、合金镀层和复合镀层三类；若按用途分类，可分为防护性镀层、防护性装饰镀层、装饰性镀层、修复性镀层、功能性镀层五种。传统电极镀层存在烧结温度过高，消耗能源致使生产成本提高的缺点。CN107274960A公开了一种无机导电电极膜及其制备方法，其采用银粉、超细云母粉、氧化铋、氧化锌、三氧化二锑、硼酸、氧化铝、氧化镁、石英砂、碳酸锂、碱式碳酸铜为原料，制得的电极膜导电性能优异，但烧结温度高于本专利技术的技术方案。
技术实现思路
针对现有技术的不足，本专利技术提供一种易烧结的电极镀层材料及其制备方法，具有优良的导电性能和易烧结的特性。本专利技术使通过以下技术方案实现的：一种易烧结的电极镀层材料，由以下原料按重量份组成：21～33份纳米铜粉、10～15份二氧化锰、6～10份氯化钴、8...
【技术保护点】
1.一种易烧结的电极镀层材料，其特征在于，由以下原料按重量份组成：21～33份纳米铜粉、10～15份二氧化锰、6～10份氯化钴、8～13份氧化镍、2～5份氧化铷、15～18份粘结剂、1～3份表面活性剂。
【技术特征摘要】
1.一种易烧结的电极镀层材料，其特征在于，由以下原料按重量份组成：21～33份纳米铜粉、10～15份二氧化锰、6～10份氯化钴、8～13份氧化镍、2～5份氧化铷、15～18份粘结剂、1～3份表面活性剂。2.根据权利要求1所述的一种易烧结的电极镀层材料，其特征在于，所述粘结剂为聚乙烯醇或羧甲基纤维素。3.根据权利要求1所述的一种易烧结的电极镀层材料，其特征在于，所述表面活性剂为脂肪醇聚氧乙烯醚硫酸钠或脂肪醇聚氧乙烯醚硫酸铵。4.权利要求1所述的一种易烧结的电极镀层材料的制备方法，其特征在于，包括以下步骤：步骤1)将粘结剂和去离子水置于反应釜中调和稀释，搅拌10～30min备用；步骤2)按重量份称取二...
【专利技术属性】
技术研发人员：汪雪婷，
申请(专利权)人：南京时恒电子科技有限公司，
类型：发明
国别省市：江苏,32