The invention discloses a preparation method of lignin based acrylate polymer by emulsion polymerization process. The lignin based acrylate polymer prepared by emulsion polymerization process is first modified by conjugated dienes and then polymerized with acrylate monomer by emulsion polymerization. Compared with traditional solvent based polymers, emulsion polymers have the advantages of environmental protection, energy saving and safety. Lignosulfonate, as a useless byproduct of pulp and paper making, has been used as a macromonomer to graft with acrylic monomers. It has found a new application direction for lignosulfonate obtained from pulping and papermaking, and also reduced the cost of pure acrylate emulsion.
【技术实现步骤摘要】
木质素磺酸盐-二烯酸-丙烯酸酯共聚乳液的制备方法
本专利技术涉及一种由共轭二烯酸、木质素磺酸盐、丙烯酸酯类单体制备木质素基丙烯酸酯乳液的方法。
技术介绍
当今社会，人们对能源的需求日益增长，不可再生的石化资源的日益枯竭，再加之化石能源的无节制开采源于石化资源的化工原材料的使用不具有可持续性，使用生物质可再生化合物用于制备各种化合物的方法正日益受到重视。自然界中木质素的储量仅次纤维素，而且每年以500亿吨的速度再生。而木质素绝少得到高效利用。因此，利用木质素代替部分石油化工产品合成高分子具有重大的理论意义和实践意义。木质素本身反应活性很低，在工业化的利用方面一直受到限制。木质素难以利用是其结构与性能决定的。木质素是聚酚类三维网状高分子化合物，木质素结构主体间的连接方式主要是醚键和碳碳双键，这两种化学键极性小、键能高，难以反应，而且甲氧基的含量高，羟基的含量低，酚羟基邻位缺乏反应活性点，不利于缩聚、接枝和磺化等反应的进行。刘晓欢用丙烯酰氯改性木质素，然后通过自由基与丙烯酸正丁酯和甲基丙烯酸甲酯在有机相中共聚，制得了良好的耐化学性，热性能和机械性能的聚合物。Nigel等...
【技术保护点】
1.由乳液聚合的工艺制备木质素基丙烯酸酯聚合物方法，其特征在于：先将超滤膜提纯后的木质素磺酸盐超声溶解于N，N‑二甲基乙酰胺中，再在超临界二氧化碳条件下将木质素磺酸与共轭二烯酸酯化，得到产物与丙烯酸酯类单体经氧化还原引聚合制得木质素基丙烯酸酯乳液。
【技术特征摘要】
1.由乳液聚合的工艺制备木质素基丙烯酸酯聚合物方法，其特征在于：先将超滤膜提纯后的木质素磺酸盐超声溶解于N，N-二甲基乙酰胺中，再在超临界二氧化碳条件下将木质素磺酸与共轭二烯酸酯化，得到产物与丙烯酸酯类单体经氧化还原引聚合制得木质素基丙烯酸酯乳液。2.如权利要求1所述的木质素基丙烯酸酯聚合物的制备方法，其特征在于：所述的木质素磺酸盐是经超滤膜分级提纯后得到分子量在400-600的木质素磺酸盐。3.如权利要求1所述的木质素基丙烯酸酯聚合物的制备方法，其特征在于：超临界酯化条件为温度50～70℃，压力15～30MPa，时间3～5h。4.如权利要求1所述的木质素基丙烯酸酯聚合物的制备方法，其特征在于：共轭二烯酸为己二烯酸、庚二烯酸、...
【专利技术属性】
技术研发人员：金立维，张永贺，王春鹏，储富祥，
申请(专利权)人：中国林业科学研究院林产化学工业研究所，
类型：发明
国别省市：江苏,32