The invention discloses a polycarboxylic acid water reducer and a preparation method. The water reducer has good mud resistance and low dosage. A polycarboxylic acid water reducer was prepared from 330 parts of polyoxyethylene methacrylate, 10 parts of acrylic acid, 15 parts of hydroxyethyl acrylate, 3 parts of citric acid, 1 part of tartaric acid, 2 parts of mercaptopropanol, 5 parts of sodium methacrylate, 3 parts of ammonium persulfate, 1 part of potassium dichromate and polypropylene. Olefinamide 0.5 1, potassium persulfate 1 4, sodium hydroxide and deionized water are appropriate. The superplasticizer has the advantages of high dispersibility and retention of particles, low cost, strong adaptability of concrete, good mud resistance, good workability, good slump retention and stable quality.
【技术实现步骤摘要】
一种聚羧酸减水剂及制备方法
本专利技术一种聚羧酸减水剂及制备方法，属于减水剂
技术介绍
聚羧酸减水剂是制备高性能混凝土的基础材料，具有高减水率、高保坍性、高增强以及高耐久等优良性能，聚羧酸减水剂能减少拌合用水量、提高混凝土强度，被越来越广泛地应用于混凝土工程中。然而由于生产混凝土用的原材料种类繁多，地区差异大，造成了聚羧酸减水剂在实际应用中出现各种不适应性问题，比如表现为混凝土坍落度经时损失过快、泌水离析现象严重、敏感度高等等。以上问题严重影响混凝土的正常施工，为工程质量带来隐患。大量的工程实例及研究表明，粘土矿物会导致混凝土强度及耐久性下降，显著降低减水剂的分散性能，特别是聚羧酸减水剂。聚羧酸减水剂与混凝土原材料之间的适应性一直是制约聚羧酸减水剂广泛适用的一个重要原因。为解决聚羧酸减水剂这方面不足，急需开发一种新的聚羧酸减水剂，不仅需要具有传统减水剂的工作性能，同时还需要抵抗粘土，克服碱矿渣急凝、保坍效果等特征。
技术实现思路
为解决现有技术存在的不足，本专利技术公开了一种聚羧酸减水剂及制备方法，该产品混凝土适应性强、成本低廉、抗泥性好、混凝土和易性好、保...
【技术保护点】
1.一种聚羧酸减水剂，其特征在于，由以下重量份的原料制备得到：甲基烯丙醇聚氧乙烯醚330‑370份、丙烯酸10‑30份、丙烯酸羟乙酯15‑30份、柠檬酸3‑10份、酒石酸1‑5份、巯基丙醇2‑3份、甲基丙烯磺酸钠5‑10份、过硫酸铵3‑5份、重铬酸钾1‑5份、聚丙烯酰胺0.5‑1份、过硫酸钾1‑4份、氢氧化钠和去离子水适量。
【技术特征摘要】
1.一种聚羧酸减水剂，其特征在于，由以下重量份的原料制备得到：甲基烯丙醇聚氧乙烯醚330-370份、丙烯酸10-30份、丙烯酸羟乙酯15-30份、柠檬酸3-10份、酒石酸1-5份、巯基丙醇2-3份、甲基丙烯磺酸钠5-10份、过硫酸铵3-5份、重铬酸钾1-5份、聚丙烯酰胺0.5-1份、过硫酸钾1-4份、氢氧化钠和去离子水适量。2.根据权利要求1所述的一种聚羧酸减水剂，其特征在于，由以下重量份的原料制备得到：甲基烯丙醇聚氧乙烯醚340-360份、丙烯酸15-25份、丙烯酸羟乙酯20-30份、柠檬酸5-8份、酒石酸2-4份、巯基丙醇2-3份、甲基丙烯磺酸钠6-8份、过硫酸铵3-4份、重铬酸钾2-4份、聚丙烯酰胺0.7-0.9份、过硫酸钾2-3份、氢氧化钠和去离子水适量。3.权利要求1或2所述的聚羧酸减水剂的制备方法，其特征在于，包括以下步骤：1）配液：配置A液：准确称取丙...
【专利技术属性】
技术研发人员：张志民，张鹏，张博，
申请(专利权)人：山西奥瑞特建材科技有限公司，
类型：发明
国别省市：山西,14