The invention belongs to the technical field and proposes a high strength waterborne epoxy waterproof coating, which comprises component A and component B. The component A includes the following components of mass ratio: waterborne epoxy resin 90 100, dispersant 0.4 0.6, wetting agent 0.1 0.5, defoamer 1 2, water 30 35. The component B includes the following components of mass ratio: modified polyether amine curing agent 15 20, calcium magnesium powder. 10_25, fiber powder 5_10, quartz powder 3_6, wollastonite 6_8, silane coupling agent 0.01_0.02, polyurethane 10_15. The invention also provides a preparation method of high strength waterborne epoxy waterproof coating. Through the above technical scheme, the problem of low strength and unstable storage of waterproof coating in the prior art is solved.
【技术实现步骤摘要】
一种高强度水性环氧防水涂料及其制备方法
本专利技术属于防水涂料
，涉及一种高强度水性环氧防水涂料。
技术介绍
防水涂料经固化后形成的防水薄膜具有一定的延伸性、弹塑性、抗裂性、抗渗性及耐候性，能起到防水、防渗和保护作用。防水涂料有良好的温度适应性，操作简便，易于维修与维护。近年来，我国防水涂料的研制取得了很大进步，在以后的发展过程中高耐候、环保型和多功能防水涂料是未来防水涂料的发展方向。CN103694855B公开了水性环氧防水涂料及其制备方法，专利技术的水性环氧防水涂料由组分A、组分B和组分C构成，其主要成膜物质是由组分A中的低分子双酚A环氧树脂和改性环氧树脂在一定工艺下分散而成，其固体份环氧值在0.36-0.44，具有较高环氧值；固化后的漆膜有高交联密度，高硬度的特点；以及极好的耐水、耐化学品性能；组分B中的轻质材料可减轻墙体对防水涂料的承重载荷以及可获得较好的保温效果，其适用于保温体系的外墙防水施工及室内防水施工。组分B中的水溶性聚磷酸铰为短链低聚合度多磷酸铰，其与组分A、组分C混合分散成膜后，具有较高的阻燃效果。但是该专利技术在使用过程中存在敲打强度低...
【技术保护点】
1.一种高强度水性环氧防水涂料，其特征在于：包括A组分和B组分，所述A组分包括以下质量配比的组分：水性环氧树脂90‑100，分散剂0.4‑0.6，润湿剂0.1‑0.5，消泡剂1‑2、水30‑35，所述B组分包括以下质量配比的组分：改性聚醚胺固化剂15‑20，钙镁粉10‑25、纤维粉5‑10、石英粉3‑6、硅灰石6‑8、硅烷偶联剂0.01‑0.02、聚氨酯10‑15。
【技术特征摘要】
1.一种高强度水性环氧防水涂料，其特征在于：包括A组分和B组分，所述A组分包括以下质量配比的组分：水性环氧树脂90-100，分散剂0.4-0.6，润湿剂0.1-0.5，消泡剂1-2、水30-35，所述B组分包括以下质量配比的组分：改性聚醚胺固化剂15-20，钙镁粉10-25、纤维粉5-10、石英粉3-6、硅灰石6-8、硅烷偶联剂0.01-0.02、聚氨酯10-15。2.根据权利要求1所述的一种高强度水性环氧防水涂料，其特征在于：包括A组分和B组分，所述A组分包括以下质量配比的组分：水性环氧树脂94，分散剂0.5，润湿剂0.3，消泡剂2、水33，所述B组分包括以下质量配比的组分：改性聚醚胺固化剂18，钙镁粉18、纤维粉7、石英粉4、硅灰石7、硅烷偶联...
【专利技术属性】
技术研发人员：杨佐林，刘建峰，白利刚，白利国，范子辕，
申请(专利权)人：广骏新材料科技有限公司，
类型：发明
国别省市：河北,13
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。