The invention provides a Nitrogen-Sulfur double-doped yellow fluorescent carbon dot and its application in anticancer drugs. The Nitrogen-Sulfur double-doped yellow fluorescent carbon dot is prepared by hydrothermal method using methyl beta cyclodextrin and methylene blue as raw materials and water as solvent. The prepared yellow fluorescent carbon dots can physically adsorb the anti-cancer drug mitoxantrone to obtain a fluorescent nano-drug system combining tracing and treatment. The nano-drug system can fluoresce mitoxantrone without affecting the anti-cancer effect of mitoxantrone. The yellow fluorescent carbon dot prepared by the invention has good water solubility, stable fluorescence performance, good biocompatibility and low toxicity, and has broad application prospects in the fields of biological imaging and drug delivery.
【技术实现步骤摘要】
一种氮、硫双掺杂黄色荧光碳点及其在抗癌药物中的应用
本专利技术涉及纳米材料及抗癌药物，具体涉及一种负载抗癌药的黄色荧光碳点及其制备方法和应用。
技术介绍
碳纳米点，也称为碳点，是一类尺寸小于10nm的新型碳纳米材料，于2004年通过电泳法净化单层碳纳米管时首次发现。由于其具有成本低、粒径小、水溶性好、化学惰性高、易功能化、抗光漂白性、无光闪烁、毒性小和生物相容性好等优点，碳点已经逐渐成为其他荧光纳米材料优良的替代品。碳点这些独特的性质使其应用于许多实际应用领域，如生物成像、药物传递、化学传感器和生物传感器、基因传递、染料敏化剂、光催化、荧光墨水和过氧化物酶模拟物等。近年来，经过研究者的不懈努力，关于碳点的制备和应用等方面的研究已经取得了很大的进展。碳点的制备方法一般可以归结为两种：化学法和物理法。化学法主要包括电化学合成，燃烧法/热/水热/酸氧化，模板合成，微波/超声辅助合成法，溶液化学合成，富勒烯开笼的方法等。物理法合成碳点主要包括电弧放电，激光烧蚀/钝化，等离子体处理等方法。然而上述方法所制备的碳点多数发射蓝色荧光，所以制备更加红移的荧光碳点可有效地避免来自生...
【技术保护点】
1.一种氮、硫双掺杂黄色荧光碳点的制备方法，其特征在于，包括如下步骤：(1)将甲基‑β‑环糊精和亚甲蓝加入去离子水中混匀，制得混合液；(2)将步骤(1)得到的混合液转移到水热反应釜中，进行水热反应；(3)将步骤(2)得到的产物经过离心、透析，最终得到氮、硫双掺杂黄色荧光碳点溶液。
【技术特征摘要】
1.一种氮、硫双掺杂黄色荧光碳点的制备方法，其特征在于，包括如下步骤：(1)将甲基-β-环糊精和亚甲蓝加入去离子水中混匀，制得混合液；(2)将步骤(1)得到的混合液转移到水热反应釜中，进行水热反应；(3)将步骤(2)得到的产物经过离心、透析，最终得到氮、硫双掺杂黄色荧光碳点溶液。2.如权利要求1所述的一种氮、硫双掺杂黄色荧光碳点的制备方法，其特征在于，步骤(1)所述的甲基-β-环糊精和亚甲蓝质量比2-4:1。3.如权利要求1所述的一种氮、硫双掺杂黄色荧光碳点的制备方法，其特征在于，步骤(1)所述的甲基-β-环糊精和亚甲蓝质量比3:1。4.如权利要求1所述的一种氮、硫双掺杂黄色荧光碳点的制备方法，其特征在于，步骤(2)所述水热反应的温度为180～250℃，持续5～25h。5.如权利要求1所述的一种氮、硫双掺杂黄色荧光碳点的制备方法，其特征在于，步骤(3)所述的离心是使用离心机以8000r/min转速离心8min；所述的透析...