本发明专利技术提供一种基于废弃烟梗的氮掺杂碳点的合成方法，其以废弃烟梗为碳源，以水为溶剂于反应釜中进行水热反应，反应结束后经过滤、透析、浓缩、干燥制备获得。该氮掺杂碳点表面富含羧基和氨基等官能团，平均粒径约4.7 nm，水溶性良好，在紫外光激发下可发射明亮的荧光，且具有激发依赖的荧光发射行为，可作为荧光探针应用于生物成像等方面。

A Nitrogen Doped Carbon Point Based on Abandoned Tobacco Stem and Its Synthesis Method and Application

The invention provides a synthesis method of nitrogen-doped carbon point based on waste tobacco stem, which takes waste tobacco stem as carbon source and water as solvent to conduct hydrothermal reaction in a reactor, and is prepared by filtration, dialysis, concentration and drying after reaction. The nitrogen-doped carbon dots are rich in functional groups such as carboxyl and amino groups, with an average particle size of 4.7 nm. They have good water solubility. They can emit bright fluorescence under ultraviolet excitation, and have excitation-dependent fluorescence emission behavior. They can be used as fluorescence probes in biological imaging and other fields.

【技术实现步骤摘要】
一种基于废弃烟梗的氮掺杂碳点及其合成方法和应用
本专利技术属于碳点合成
，具体涉及一种基于废弃烟梗的氮掺杂碳点及其合成方法和应用，该方法首次以卷烟生产中的废弃烟梗为碳源，采用一步水热法制备合成了发光性能优良的氮掺杂碳点。
技术介绍
烟梗是卷烟工业的副产物，约占叶重的25%~30%。烟梗中细胞壁物质含量较高，主要包括纤维素、半纤维素、果胶质和木质素，此外还有多种有效成分如烟碱、茄尼醇、绿原酸、蛋白质和氨基酸等，具有很高的利用价值。但受到现有技术的限制，目前国内每年有数十万吨的烟梗被废弃，在污染环境的同时也造成了极大的资源浪费。因此，发展新技术，拓宽烟梗的高值化利用途径，成为烟草行业新的研究热点。碳点，是一类至少有一个维度尺寸在l0nm以下且具有荧光性质的碳基纳米材料。由于碳点的原材料资源丰富，且具有优异的化学惰性、高生物相容性、良好的水溶性、发射光谱可调以及抗光漂白等优点，近年来在生物成像、生物医药、化学传感、光催化以及光电器件等方面表现出广阔的应用前景。天然生物质材料含有丰富的蛋白质、糖类及脂肪等，是用来制备碳点的理想绿色化前驱体。而采用不同碳源制备所获得的碳点，由于表面结构和本文档来自技高网...

【技术保护点】
1.一种基于废弃烟梗的氮掺杂碳点的合成方法，其特征在于，以废弃烟梗为碳源，以水为溶剂于反应釜中进行水热反应，反应结束后经过滤、透析、浓缩、干燥即得。

【技术特征摘要】
1.一种基于废弃烟梗的氮掺杂碳点的合成方法，其特征在于，以废弃烟梗为碳源，以水为溶剂于反应釜中进行水热反应，反应结束后经过滤、透析、浓缩、干燥即得。2.根据权利要求1所述基于废弃烟梗的氮掺杂碳点的合成方法，其特征在于，包括如下步骤：1）将洗净、干燥的烟梗粉末与蒸馏水混合后于反应釜中在190－210℃条件下水热反应6－12小时；2）反应结束后，自然冷却至室温，用滤纸过滤；所得滤液用截留分子量为100－500Da的透析膜透析至少48小时，获得...