A one-step preparation method of nitrogen-doped carbon quantum dots is to wash and dry plant fruits rich in various plant proteins, grind them into powder and mix them in deionized water until the powder is evenly dispersed in water. Then the dispersion system is transferred to a stainless steel autoclave lined with PTFE for hydrothermal reaction, and the product is filtered after the system is cooled to room temperature. After removing the unreacted raw materials, the filtrate was dialyzed. Finally, the liquid in the dialysis bag was dried to obtain nitrogen-doped carbon quantum dot solid powder. The invention is simple, fast, low cost, green, environmental protection and pollution-free.
【技术实现步骤摘要】
一种氮掺杂碳量子点的一步制备方法
本专利技术涉及碳量子点的制备
，特别涉及一种具有上转换发光性质的氮掺杂碳量子点的一步制备方法。
技术介绍
碳量子点是量子点的一种，是以碳为骨架的一种近似球形且直径小于10nm的零维半导体材料，相对多数以铅、镉等重金属为原料制备的量子点，碳量子点具有无毒，对环境友好，稳定性好、生物相容性好、易于功能化、荧光可调性好、抗光漂白性高等特性，从而被广泛应用于生物传感、荧光检测、生物成像、光催化剂、光电器件、生物标记等领域，受到各个研究领域的广泛关注。目前制备碳量子点的方法主要有热解法、电解法、激光法等。常用石墨烯、碳纳米管以及有机物等作为碳源，导致制备碳量子点的成本高昂。因此寻找一种原料价格便宜，碳量子点产量高、荧光性质好、制备简单环保绿色的方法，对于碳量子点在实际生产生活中的应用具有重要的意义。
技术实现思路
为了解决现有技术中的不足，本专利技术的目的在于提供一种简单快速、成本低、绿色环保无污染的氮掺杂碳量子点的一步制备方法。为了实现上述目的，本专利技术采用的技术方案如下：一种氮掺杂碳量子点的一步制备方法，包括以下步骤：（1）将富含多...
【技术保护点】
1.一种氮掺杂碳量子点的一步制备方法，其特征在于包括如下步骤：（1）将富含多种植物蛋白的植物果实洗净烘干，研磨成粉末，作为制备氮掺杂碳量子点的碳源材料；（2）将上述植物果实的细粉加入到去离子水中，使用磁力搅拌器进行搅拌，直至粉末均匀的分散于水中，然后将分散体系转移至聚四氟乙烯内衬的不锈钢高压反应釜中进行水热反应，待体系冷却至室温后，对产物进行过滤，除去未反应完全的原料，然后对滤液进行透析，最后将透析袋内液体进行干燥处理，即得氮掺杂碳量子点固体粉末。
【技术特征摘要】
1.一种氮掺杂碳量子点的一步制备方法，其特征在于包括如下步骤：（1）将富含多种植物蛋白的植物果实洗净烘干，研磨成粉末，作为制备氮掺杂碳量子点的碳源材料；（2）将上述植物果实的细粉加入到去离子水中，使用磁力搅拌器进行搅拌，直至粉末均匀的分散于水中，然后将分散体系转移至聚四氟乙烯内衬的不锈钢高压反应釜中进行水热反应，待体系冷却至室温后，对产物进行过滤，除去未反应完全的原料，然后对滤液进行透析，最后将透析袋内液体进行干燥处理，即得氮掺杂碳量子点固体粉末。2.如权利要求1所述的一种氮掺杂碳量子点的一步制备方法，其特征在于所述步骤(1)中，粉末的粒径为100～5000目。3.如权利要求1所述的一种氮掺杂碳量子点的一步制备方法，其特征在于所述步骤(2)中，植物果实细粉与去离子水的质量比为1:10-100。4.如权利要求1所述的一种氮掺杂碳量子点的一步制备方法，其特...
【专利技术属性】
技术研发人员：台秀梅，尹言吉，杜志平，王天壮，刘晓英，
申请(专利权)人：中国日用化学研究院有限公司，
类型：发明
国别省市：山西,14