The invention relates to the field of epoxy resin, in particular to an epoxy resin system for pultrusion moulding, comprising the following components: epoxy resin 100 weight parts; isocyanate curing agent 30-60 weight parts; and fluorinated epoxy compound 2-10 weight parts. It also contains 30 to 60 parts of amine curing agent, 1 to 10 parts of fluorosilicone polymer and 1 to 10 parts of accelerator. The invention also provides an epoxy resin composite material, which is prepared by an epoxy resin system for pultrusion moulding according to the invention. The epoxy resin system used in the pultrusion process of the invention has higher curing rate, and can greatly improve the traction speed in the pultrusion process, thereby improving the work efficiency. At the same time, the epoxy resin products prepared by the invention have excellent mechanical properties and good toughness.
【技术实现步骤摘要】
一种拉挤成型用环氧树脂体系及其制备的复合材料
本专利技术涉及环氧树脂领域，具体涉及一种拉挤成型用环氧树脂体系。
技术介绍
环氧树脂是优良的热固性树脂，它与不饱和聚酯树脂相比，具有更优良的物理性能、电绝缘性能、耐化学腐蚀性能、耐热和粘合性能，是目前最普遍、最重要的一种基体材料和结构材料。挤拉成型是热固性纤维增强塑料重要的加工方法之一，用于生产断面形状固定不变，长度不受限制的型材。挤拉成型工艺是将浸渍树脂胶液的连续纤维经加热模拉出，然后再通过加热室使树脂进一步固化而制备的单向高强度连续增强塑料型材。挤拉成型工艺制备的环氧树脂碳纤维增强材料一般会出现如下问题：(1)若环氧树脂固化速率过快，则会出现局部的交联，导致材料性脆；(2)若环氧树脂固化速率过慢，则可能会出现环氧树脂固化不完全，样品在卷曲、存放过程中会受力开裂的情况。所以需要根据环氧树脂的固化速率，选择合适的模具温度和牵引速度。为了进一步提高生产效率，提高牵引速度，需要环氧树脂具有固化速度快的特点，同时依然保持高强度和高韧性。
技术实现思路
为了解决上述问题，本专利技术提供了一种拉挤成型用环氧树脂体系，包含以下组分：环...
【技术保护点】
1.一种拉挤成型用环氧树脂体系，其特征在于：包含以下组分：环氧树脂100重量份；异氰酸酯类固化剂30～60重量份；含氟环氧化合物2～10重量份。
【技术特征摘要】
1.一种拉挤成型用环氧树脂体系，其特征在于：包含以下组分：环氧树脂100重量份；异氰酸酯类固化剂30～60重量份；含氟环氧化合物2～10重量份。2.根据权利要求1所述的拉挤成型用环氧树脂体系，其特征在于：所述的异氰酸酯类固化剂是4,4′-亚甲基二(2,6-二乙基苯基异氰酸酯)、赖氨酸二异氰酸酯、甲苯基-2,4-二异氰酸酯封端聚丙二醇或4-氯-6-甲基间亚苯基二异氰酸酯中的一种或多种。3.根据权利要求1所述的拉挤成型用环氧树脂体系，其特征在于：所述的含氟环氧化合物的分子量为250～400。4.根据权利要求1～3任一项所述的拉挤成型用环氧树脂体系，其特征在于：以环氧树脂100重量份计，还含有胺类固化剂30～60重量份。5.根据权利要求4所述的拉挤成型用环氧树脂体系，其特征在于：所述的胺类固化剂是N...
【专利技术属性】
技术研发人员：严兵，赵清新，张可可，施刘生，郎鸣华，何定军，张林强，刘腾达，刘圣强，
申请(专利权)人：江苏澳盛复合材料科技有限公司，
类型：发明
国别省市：江苏,32