The invention discloses an activator and its application in improving the penetration of aluminum alloy CMT welding joint. The activator consists of SiO 2, TiO 2 and CrO 3, and a layer of activator is coated on the aluminum plate before the CMT welding of the aluminum alloy. When the active agent is not applied on the weld surface, the liquid metal flows from the bottom of the weld pool to the surface of the weld pool. When the active agent is applied on the weld surface, the flow direction of the liquid metal changes and flows from the surface of the weld pool to the bottom of the weld pool, resulting in arc contraction. At the same time, the increase of electromagnetic force and the change of the surface tension gradient of the weld pool from negative value to positive value increase the penetration.
【技术实现步骤摘要】
活性剂及其在改善铝合金CMT焊接头熔深中的应用
本专利技术属于焊接
，更加具体地说，涉及利用涂敷活性剂的方法，改善铝合金CMT焊接头熔深。
技术介绍
冷金属过渡技术(ColdMetalTransfer，CMT)是奥地利福尼斯公司在钢与铝焊接、无飞溅引弧技术以及微连接技术基础之上开发的一种低热输入量的焊接技术。CMT技术的创新之处在于将熔滴过渡与送丝过程结合，从而降低了焊接过程的热输入量，真正实现了无飞溅焊接。由于CMT焊接过程热输入低，导致CMT焊接头熔深浅，仅能焊接薄板，应用范围受限。
技术实现思路
本专利技术的目的在于克服现有技术的不足，提供活性剂及在改善铝合金CMT焊接头熔深中的应用，可以有效的增加接头熔深。本专利技术的技术目的通过下述技术方案予以实现：活性剂，由二氧化硅、二氧化钛和三氧化二铬组成，二氧化硅、二氧化钛和三氧化二铬均为纯度大于等于99％的粉末，粒径为100—500目，优选200—300目；二氧化硅、二氧化钛和三氧化二铬的质量比(2—5)：(1—2)：(1—2)，优选(2—4)：(1—1.5)：(1—1.5)，二氧化钛和三氧化二铬为等质量比。在...
【技术保护点】
1.活性剂，其特征在于，由二氧化硅、二氧化钛和三氧化二铬组成，二氧化硅、二氧化钛和三氧化二铬均为纯度大于等于99％的粉末，粒径为100—500目；二氧化硅、二氧化钛和三氧化二铬的质量比(2—5)：(1—2)：(1—2)，二氧化钛和三氧化二铬为等质量比。
【技术特征摘要】
1.活性剂，其特征在于，由二氧化硅、二氧化钛和三氧化二铬组成，二氧化硅、二氧化钛和三氧化二铬均为纯度大于等于99％的粉末，粒径为100—500目；二氧化硅、二氧化钛和三氧化二铬的质量比(2—5)：(1—2)：(1—2)，二氧化钛和三氧化二铬为等质量比。2.根据权利要求1所述的活性剂，其特征在于，粒径为200—300目。3.根据权利要求1所述的活性剂，其特征在于，二氧化硅、二氧化钛和三氧化二铬的质量比为(2—4)：(1—1.5)：(1—1.5)。4.如权利要求1或者2或者3所述的活性...
【专利技术属性】
技术研发人员：胡绳荪，田银宝，申俊琦，王志江，白鹏飞，
申请(专利权)人：天津大学，
类型：发明
国别省市：天津,12