The invention relates to an antibacterial cotton-linen blending technology, which is characterized in that the blending textile process comprises the following steps: (1) measuring the maximum tensile strength of the linen fiber, i.e. the maximum applied pressure on it; (2) placing the cotton fiber in a water steaming tank at a water temperature of 70-75 (?) and steaming for 60-70 minutes; (3) treating the linen fiber with the steps (2) The cotton filament is preset for 16-18 hours in the natural state; (4) Mixed spinning of cotton filament and linen filament is carried out by water-jet loom with step (1) maximum pressure value; among them, the nozzle of 7582 The invention has the advantages that the quality of the final woven product is unsatisfactory due to the different characteristics of the cotton fiber and the flax fiber when the cotton fiber and the flax fiber are mixed for spinning.
【技术实现步骤摘要】
一种抗菌棉麻混纺技术
本专利技术涉及混纺
，尤其涉及一种抗菌棉麻混纺技术。
技术介绍
利用不同原料丝进行混合纺织时，各种原料丝的张力及适宜加工温度等都是影响最后成品质量的重要参数，因此在设计纺织工艺时需要照顾到不同原料丝的特性。比如我们利用棉纤维丝和麻纤维丝混合纺织成织物时，由于棉纤维丝和麻纤维丝特性区别较大，就需采用特定工艺进行纺织。具体地，麻纤维丝柔软舒适，吸湿性好，但弹性恢复能力弱；而棉纤维丝耐热水性好，弹性恢复能力好。将上述棉纤维丝和麻纤维丝进行混合纺织时为了照顾不同原料丝的特性以保证最后成品的质量，目前本企业采用的方法是：利用喷水织机对棉纤维丝和麻纤维丝进行牵引时均采用相同的规格为45-20的喷嘴；以及在进行混纺前对棉纤维丝进行预处理即将棉纤维丝放入蒸箱中，依次进行抽真空、加温、抽真空、再加温并使温度保持在85℃蒸一段时间后取出自然定型。但是，采用上述牵引与预处理工艺其效果仍然不尽如人意，最后织成的产品仍会出现较多的挡子。综上所述，亟待解决的问题是，利用棉纤维丝和麻纤维丝进行混合纺织时需要对其纺织工艺进行改进，以克服上述缺点。
技术实现思路
本专利技术...
【技术保护点】
1.一种抗菌棉麻混纺技术，其特征在于：所述混合纺织工艺包括如下步骤：(1)测出麻纤维丝可拉伸的最大限度即对其可施加的最大压力值；(2)将棉纤维丝置于水蒸箱中，水温70～75℃，蒸60～70分钟；(3)将步骤(2)处理后的棉纤维丝置于自然状态下预定型10～ 12小时；(4)采用喷水织机以步骤(1)最大压力值对棉纤维丝与麻纤维丝进行混合纺织；其 中，喷水织机对棉纤维丝进行牵引时采用规格为75‑40的喷嘴，对麻纤维丝进行牵引时采用 规格为45‑20的喷嘴。
【技术特征摘要】
1.一种抗菌棉麻混纺技术，其特征在于：所述混合纺织工艺包括如下步骤：(1)测出麻纤维丝可拉伸的最大限度即对其可施加的最大压力值；(2)将棉纤维丝置于水蒸箱中，水温70～75℃，蒸60～70分钟；(3)将步骤(2)处理后的棉纤维丝置于自然状态下预定型10～12小时；(4)采用喷水...
【专利技术属性】
技术研发人员：吴训华，
申请(专利权)人：如皋市丹凤纺织有限公司，
类型：发明
国别省市：江苏,32