一种消除冷轧普板连续退火带钢表面麻点的方法技术

本发明专利技术涉及了一种消除冷轧普板连续退火带钢表面麻点的方法，根据带钢表面麻点缺陷微观特点，结合生产现场深入分析连退炉炉辊结瘤微观特征及其形成机理，采取如下措施消除炉辊表面结瘤从而保证带钢表面质量：控制原料带钢表面残铁量≤50mg/m

A method to eliminate surface pitting on cold rolled strip continuous annealing strip

The present invention relates to a method for eliminating surface pitting of cold rolled strip annealed continuously. According to the microscopic characteristics of surface pitting defect of strip steel, combining with in-depth analysis of the microscopic characteristics and forming mechanism of the nodulation of the furnace roll on the production site, the following measures are taken to eliminate the surface pitting of the furnace roll so as to ensure the surface quality of the strip steel: The residual iron content of material strip is less than 50mg/m

【技术实现步骤摘要】
一种消除冷轧普板连续退火带钢表面麻点的方法
本专利技术属于材料加工工程
，涉及了一种消除冷轧普板连续退火带钢表面麻点的方法。
技术介绍
表面质量是影响普板连退带钢产品质量的一个重要方面，尤其是带钢麻点缺陷，厚规格尤为严重。带钢麻点问题不仅影响成品合格率还影响连退机组的正常生产。真彩共聚焦显微镜检测分析表明，麻点深度在20-30μm左右。根据麻点表现形式可以将麻点分为：针点状、短线状、白点状和颗粒物压印几种类型；跟踪表明带钢表面麻点缺陷主要由炉辊结瘤和炉内颗粒物压印导致。连退炉炉辊结瘤形成机制主要由以下两种：①带钢表面的氧化物、铁屑等在辊子表面还原和粘结聚集；由于炉辊磨损，部分区域变得粗糙。在高温并带张力和摩擦力环境下，带钢上熔融、粘结的氧化物颗粒和铁粉在辊子表面粗糙度较大地方堆积，层层累加，从而形成结瘤。②炉内颗粒物在炉辊表面附着、聚集并粘附在炉辊辊面形成结瘤。专利CN103710518A公布了一种通过控制炉辊结瘤来消除钢板辊印的方法，采用高温板和低温板循环生产以及厚钢板快速通炉吸热降温，控制炉辊上瘤渣的长大和消除，从而降低停炉频次，提高炉子作业率。所述方法仅适用于热轧钢板热处本文档来自技高网...

【技术保护点】
1.一种消除冷轧普板连续退火带钢表面麻点的方法，冷轧普板连续退火带钢的生产工艺流程包括：炼钢‑>连铸‑>热轧‑>酸洗‑>五机架冷连轧‑>脱脂清洗‑>‑>漂洗‑>热风烘干‑>连续退火‑>卷取，其特征在于：(1)控制原料带钢表面残铁量≤50mg/m2；(2)控制脱脂液浓度25‑27g/L，脱脂液铁粉含量≤100mg/kg，漂洗液铁粉含量≤30mg mg/Kg；(3)连续退火炉炉辊涂层采用超音速喷涂、炉辊辊面粗糙度(Ra)5～7μm；(4)控制连续退火炉炉区各段张力差≤3KN。

【技术特征摘要】
1.一种消除冷轧普板连续退火带钢表面麻点的方法，冷轧普板连续退火带钢的生产工艺流程包括：炼钢->连铸->热轧->酸洗->五机架冷连轧->脱脂清洗->->漂洗->热风烘干->连续退火->卷取，其特征在于：(1)控制原料带钢表面残铁量≤50mg/m2；(2)控制脱脂液浓度25-27g/L，脱脂液铁粉含量≤100mg/kg，漂洗液铁粉含量≤30mgmg/Kg；(3)连续退火炉...

【专利技术属性】
技术研发人员：关建辉，孙林，丁美良，孙兴，
申请(专利权)人：江苏省沙钢钢铁研究院有限公司，张家港扬子江冷轧板有限公司，江苏沙钢集团有限公司，
类型：发明
国别省市：江苏,32