The invention relates to a ready-mixed sea sand masonry mortar material and a preparation method thereof. The raw sea sand and manufactured sand are mixed as fine aggregate, and cement, fly ash, cellulose ether and mixing water are added. The mass ratio of cement to fly ash is 1:0.3, and the total mass ratio of cement to manufactured sand and raw sea sand is 1:4.8. The mass ratio of sand making to sea sand (0-0.5), cement to water (1:0.9), cellulose ether (0.15%) as cementitious material (cement and fly ash). The invention has the uniqueness of raw material selection, simple preparation method, no special process, is suitable for large-scale industrial production, easy to produce scale benefit and low cost. The ready-mixed mortar mixed with sea sand mixed with manufactured sand has excellent basic properties such as consistency, 2H consistency loss, shrinkage, 28d compressive strength, flexural strength and tensile bond strength.
【技术实现步骤摘要】
预拌海砂砌筑砂浆材料及其制备方法
本专利技术属于建筑材料
，具体涉及一种预拌海砂砌筑砂浆材料及其制备方法。
技术介绍
砌筑砂浆指的是将砖、石、砌块等块材经砌筑成为砌体的砂浆。它在砌体中起粘结、衬垫和传力作用，是砌体的重要组成部分，在建筑工程中有较大的用量和不可或缺的地位。预拌砂浆是指由专业化厂家生产的，用于建设工程中的各种砂浆拌合物。作为典型的商品砂浆品种，预拌砂浆在欧洲许多国家的应用已经非常普遍，在亚洲的发展也十分迅速，而我国在这方面的研发和推广工作刚刚开始。目前，预拌砂浆的应用主要集中在北京、上海、广东等一线城市。上海地区是最早禁止使用现拌砂浆的，采用预拌湿砂浆为主、干粉砂浆为辅的策略，并拟采取强制性推广措施，就是为了减少现拌砂浆造成的粉尘污染和噪声污染，保障施工质量。和传统的现拌砂浆相比，预拌砂浆不但克服了传统现场搅拌砂浆带来的开裂、空鼓、脱落、渗漏、强度较低且不稳定等问题，而且具有计量精确，有规模效应、节约原材料、效率高、对周围环境影响小、人工成本低的特点，有较高的科技附加值。建筑工程中，砂浆的用量仅次于混凝土，但与混凝土相比，海砂在砂浆中应用的研究...
【技术保护点】
1.预拌海砂砌筑砂浆材料，其特征在于：利用原状海砂和机制砂混掺作为细骨料，还添加有水泥、粉煤灰、纤维素醚和拌合水；其中：水泥与粉煤灰的质量比为1：0.3，水泥与机制砂和原状海砂的总质量比为1：4.8，机制砂与海砂质量比为（0~0.5），水泥与水的质量比为1：0.9，纤维素醚为胶凝材料（水泥和粉煤灰）总质量的0.15%。
【技术特征摘要】
1.预拌海砂砌筑砂浆材料，其特征在于：利用原状海砂和机制砂混掺作为细骨料，还添加有水泥、粉煤灰、纤维素醚和拌合水；其中：水泥与粉煤灰的质量比为1：0.3，水泥与机制砂和原状海砂的总质量比为1：4.8，机制砂与海砂质量比为（0~0.5），水泥与水的质量比为1：0.9，纤维素醚为胶凝材料（水泥和粉煤灰）总质量的0.15%。2.根据权利要求1所述的预拌海砂砌筑砂浆材料，其特征在于：所述原状海砂的自由氯离子含量测定为0.12%。3.一种如权利要求1所述的预拌海砂砌筑砂浆材料的制备方法，其特征在于：具体步骤如下：按照原料配比称重，将原状海砂自然晾干，过4.75mm的圆孔筛，筛掉贝壳及大颗粒杂质；通过向原状海砂中掺杂机制砂配制成级配优良的骨料；同时将水泥、粉煤灰和拌合水放入搅拌机中，搅拌1...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。