The invention provides a two component modified polyether sealant and a preparation method thereof. The sealant provided by the invention comprises material A and material B; material A includes silane modified polyether, first plasticizer, first filler, ultraviolet absorber, light stabilizer, thixotropic agent, acrylic resin and glass microsphere; the silane modified polyether is selected from methylsilyl polyether with trimethoxy terminal group and methyldimethoxy terminal group. One or more of silane polyethers; B material includes curing agent, curing accelerator, second plasticizer and second filler; the curing agent is organotin curing agent; the curing accelerator is amine accelerator; the mass ratio of A material to B material is 100:4-15. The combination of A and B can shorten the curing period of the sealant and prolong the operation time.
【技术实现步骤摘要】
一种双组份改性聚醚密封胶及其制备方法
本专利技术涉及密封胶
，特别涉及一种双组份改性聚醚密封胶及其制备方法。
技术介绍
密封胶是装配式建筑的必要材料，主要用来对装配式建筑密封防水。装配式建筑由来已久，17世纪向美洲移民时期所用的木构架拼接房屋，就是一种装配式建筑。1851年伦敦建成的用铁骨架嵌玻璃的水晶宫是世界上第一座大型装配式建筑，第二次世界大战后，欧洲国家以及日本等国房荒严重，迫切要求解决住宅问题，促进了装配式建筑的发展。到60年代，装配式建筑得到大量推广。早在60年前，我国亦已开始探索预制装配式(PC)建筑，但是由于技术不够成熟、缺乏配套标准等问题，导致我国工业化进程缓慢甚至停滞不前。而近几年出台了一些相关政策，例如在2015年11月14日住建部出台的《建筑产业现代化发展纲要》计划到2020年装配式建筑占新建建筑的比例在20％以上，到2025年装配式建筑占新建筑的比例在50％以上；2016年2月22日国务院出台的《关于大力发展装配式建筑的指导意见》要求因地制宜发展装配式混凝土结构、钢结构和现代木结构等装配式建筑，力争用10年左右的时间，使装配式建筑占新...
【技术保护点】
1.一种双组份改性聚醚密封胶，其特征在于，包括A料和B料；所述A料包括以下重量份的组分：
【技术特征摘要】
1.一种双组份改性聚醚密封胶，其特征在于，包括A料和B料；所述A料包括以下重量份的组分：所述硅烷改性聚醚选自端基为三甲氧基的甲硅烷基聚醚和端基为甲基二甲氧基的甲硅烷基聚醚中的一种或几种；所述B料包括以下重量份的组分：所述固化剂为有机锡固化剂；所述固化促进剂为胺类促进剂；所述A料与B料的质量比为100∶(4～15)。2.根据权利要求1所述的密封胶，其特征在于，所述硅烷改性聚醚的粘度为1000～20000mPa.s。3.根据权利要求1或2所述的密封胶，其特征在于，所述端基为三甲氧基的甲硅烷基聚醚选自S510H聚醚和S520H聚醚中的一种或几种；所述端基为甲基二甲氧基的甲硅烷基聚醚选自S203H聚醚、S303H聚醚、S810H聚醚、S5830聚醚和S888聚醚中的一种或几种。4.根据权利要求1所述的密封胶，其特征在于，所述有机锡固化剂选自2-乙基己酸锡(Ⅱ)和二月桂酸二丁基锡中的一种或几种；所述胺类促进剂选自三乙烯十二胺和十二烷基伯胺中的一种或几种。5.根据权利要求1所述的密封胶，其特征在...
【专利技术属性】
技术研发人员：刘伟明，陈军，沈峰，陈丹，刘明，何永富，
申请(专利权)人：杭州之江新材料有限公司，杭州之江有机硅化工有限公司，
类型：发明
国别省市：浙江,33