The invention relates to the technical field of polymer materials, in particular to a polyester film. The polyester film is made of 60 80 parts of polyester luminous material, 20 30 parts of special masterbatch for film grade, 2 9 parts of polyorganosiloxane, 4 12 parts of solvent, 2 4 parts of trimethylphenyl phosphate, 1 3 parts of curing agent, 1 2 parts of lotus leaf alkali and 2 3 parts of fluzoxachlor. First, all the raw materials are mixed evenly by mixer, and then melted and extruded by extruder. Then the polyester film is made by longitudinal and transverse stretching. Finally, the package is rolled up. By reasonably designing components and processing technology, the invention makes the product have better light transmittance, at the same time, it has better anti-ultraviolet effect and better product quality.
【技术实现步骤摘要】
一种聚酯薄膜
本专利技术涉及高分子材料
，具体涉及一种聚酯薄膜。
技术介绍
聚酯薄膜一般是以聚对苯二甲酸乙二醇酯为原料，采用挤出法制成厚片，再经双向拉伸制成的薄膜材料。聚酯薄膜可制成环保胶片、PET胶片、乳白胶片等印刷包装耗材，广泛用于玻璃钢行业、建材行业、印刷行业、医药卫生行业等。现有聚酯薄膜的主要缺点在于透光率低，抗紫外线效果差等。
技术实现思路
为了解决现有技术中存在的技术问题，本专利技术提出了一种聚酯薄膜，具有优异的抗紫外线效果。本专利技术的技术方案是：一种聚酯薄膜，由如下重量份的原料制成：聚酯光料60-80份、膜级专用母料20-30份、聚有机硅氧烷2-9份、溶剂4-12份、磷酸三甲苯酯2-4份、固化剂1-3份、荷叶碱1-2份和氟唑草胺2-3份。作为本专利技术的优选实施例，由如下重量份的原料制成：聚酯光料66份、膜级专用母料24份、聚有机硅氧烷8份、溶剂6份、磷酸三甲苯酯3份、固化剂2份、荷叶碱1.5份和氟唑草胺2.8份。一种制备聚酯薄膜的方法，首先将所有原料经过混料机混合均匀，经过挤出机熔融挤出；然后通过纵向拉伸和横向拉伸制成聚酯薄膜，最后收卷包装即可...
【技术保护点】
1.一种聚酯薄膜，其特征在于，由如下重量份的原料制成：聚酯光料60‑80份、膜级专用母料20‑30份、聚有机硅氧烷2‑9份、溶剂4‑12份、磷酸三甲苯酯2‑4份、固化剂1‑3份、荷叶碱1‑2份和氟唑草胺2‑3份。
【技术特征摘要】
1.一种聚酯薄膜，其特征在于，由如下重量份的原料制成：聚酯光料60-80份、膜级专用母料20-30份、聚有机硅氧烷2-9份、溶剂4-12份、磷酸三甲苯酯2-4份、固化剂1-3份、荷叶碱1-2份和氟唑草胺2-3份。2.如权利要求1所述的聚酯薄膜，其特征在于，由如下重量份的原料制成：聚酯光料6...
【专利技术属性】
技术研发人员：周贤敏，
申请(专利权)人：重庆新康意安得达尔新材料有限公司，
类型：发明
国别省市：重庆,50