The invention discloses a low alloy wear resistant steel. The weight percentage of the alloy consists of carbon 3.50-4.50%, tungsten 0.8-1.3%, copper 1.3-2.50%, rare earth 0.9-2.0%, manganese 1.3-1.8%, chromium 2-3%, silicon 2.5-3.7%, vanadium 0.9-1.8%, boron 0.3-0.6% and iron. It has the following beneficial effects: because the content of carbon is reasonably limited and the ratio between chromium, nickel and carbon is specifically limited, at the same time, the appropriate proportion of other material components are selected, the protective plate produced has very high hardness, more importantly, good toughness, wear resistance, impact resistance and other properties, full The processing technology adopted in the present invention improves the microstructure and properties of the alloy by means of strong wind rapid cooling and reasonable quenching technology, and finally makes its hardness HRC67-75, good impact toughness and comprehensive mechanical properties.
【技术实现步骤摘要】
一种低合金耐磨钢
本专利技术涉及一种抛丸室用护板钢材，特别是一种低合金耐磨钢。
技术介绍
抛丸机是利用高速旋转的抛丸器将弹丸高速喷出，使弹丸具有一定的动能，高速直线运动的弹丸直接冲击在工件表面上，以清除工件表面的锈迹，但是抛丸机在进行抛丸的过程中会有弹丸绕过工件打在抛丸机的室体内，时间久了高速的弹丸会将室体打穿，因此现有技术中常常在抛丸机室体内铺设护板，现有的护板种类比较多，一般采用高铬铸铁或锰钢板，但是在面临着高速喷射的弹丸，现有的护板由于材料问题使其的强度仍然不够好，使用寿命不长，因此使用一段时间后就要将其更换，由此不但造成成本上的浪费而且耽误工期，影响生产效率。
技术实现思路
本专利技术要解决的技术问题是提供一种耐磨性好、抗冲击能力强且使用寿命长的低合金耐磨钢。为了解决上述技术问题，本专利技术的低合金耐磨钢，其重量百分比的合金成分为：碳３.５０～４.５０%，钨０.８～１.３%，铜１.3～２.50%，稀土０.９～2.０%，锰１.３～1.８%，铬２～３%，硅2.５～3.７%，钒0.９～１.8%，硼0.３～０.６%，余量为铁。2、按照权利要求1所述的低合金耐磨钢，其特...
【技术保护点】
1.一种低合金耐磨钢，其特征在于：其重量百分比的合金成分为：碳３.５０～４.５０%，钨０.８～１.３%，铜１.3～２. 50%，稀土０.９～2.０%，锰１.３～1.８%，铬２～３%，硅2.５～3.７%，钒0.９～１.8%，硼0.３～０.６%，余量为铁。
【技术特征摘要】
1.一种低合金耐磨钢，其特征在于：其重量百分比的合金成分为：碳３.５０～４.５０%，钨０.８～１.３%，铜１.3～２.50%，稀土０.９～2.０%，锰１.３～1.８%，铬２～３%，硅2.５～3.７%，钒0.９～１.8%，硼0.３～０.６%，余量为铁。2.按照权利要求1所述的低合金耐磨钢，其特征在于：其重量百分比的合金成分为：碳４%，钨１.１%，铜１.８%，稀土１.５%，锰...
【专利技术属性】
技术研发人员：张长凤，
申请(专利权)人：镇江苏佰鑫工程机械有限公司，
类型：发明
国别省市：江苏,32