The invention discloses a production process of anti-corrosion and flame retardant wood doors, including the main steps of wood spray drying pretreatment, flame retardant antiseptic configuration, wood modification, wooden door frame molding, door core sizing, door core curing and wood door assembly, etc. The invention added silver ions and nano silver in the flame retardant and the door core slurry, which greatly enhanced the antibacterial ability of the wooden doors, slowed down the decay speed of the wooden doors, and the door was sandwich structure, not only the sound insulation and heat preservation effect was good, but also the wood was saved, and the green color and environmental protection concept was conformed to.
【技术实现步骤摘要】
一种防腐阻燃木门的生产工艺
本专利技术涉及一种木门生产工艺，尤其是一种防腐阻燃木门的生产工艺。
技术介绍
千年来木材一直都是人类建造房屋打造家居的重要材料，制造门窗就是其中最重要的应用方向之一。随着经济的发展和人民生活水平的提高，人们不仅重视木门的质量和实用性，同时对其整体的美观性和安全性也有了更高的期待。现有的木门生产工艺比较简单，而且由于材质原因，其防腐阻燃性能远不及金属门，影响其使用寿命和整体的美观。但是，木门由于其不同于金属门的质感，在可预见的将来都不会被淘汰，因此人们需要对其材质进行改善来提高其防腐阻燃性能。
技术实现思路
为了克服木门易腐烂易燃烧的弊端，本专利技术提供一种防腐阻燃木门的生产工艺，并在其结构中掺杂的银离子和纳米银，和现有技术相比大幅度提升了木门的防腐能力。本专利技术解决其技术问题所采用的技术方案是：一种防腐阻燃木门的生产工艺，具体步骤如下：步骤一，将选用的木材放入干燥窑中进行喷蒸和加热干燥，喷蒸时间为10～20分钟，加热干燥时间为15～25天，至干燥后的木材含水量8～12％，保存备用；步骤二，在搅拌器中按如下质量份数比例加入原料：搅拌20～4...
【技术保护点】
1.一种防腐阻燃木门的生产工艺，具体步骤如下：步骤一，将选用的木材放入干燥窑中进行喷蒸和加热干燥，喷蒸时间为10～20分钟，加热干燥时间为15～25天，至干燥后的木材含水量8～12％，保存备用；步骤二，在搅拌器中按如下质量份数比例加入原料：
【技术特征摘要】
1.一种防腐阻燃木门的生产工艺，具体步骤如下：步骤一，将选用的木材放入干燥窑中进行喷蒸和加热干燥，喷蒸时间为10～20分钟，加热干燥时间为15～25天，至干燥后的木材含水量8～12％，保存备用；步骤二，在搅拌器中按如下质量份数比例加入原料：搅拌20～40分钟，使之均匀混合，干燥，球磨30～90分钟，得到阻燃防腐剂粉体，保存备用；步骤三，将步骤二得到的阻燃防腐剂用水稀释至质量百分比溶度为10～20％混合浸渍液，保存备用；步骤四，将步骤一得到的干燥木材放入真空浸渍釜中，抽真空，保持釜内的真空度在-0.05～-0.1MPa之间，维持30～60分钟，再将步骤三得到的混合浸渍液注入到真空浸渍釜中，将木材完全浸没，然后将真空浸渍釜恢复常压，并加热至40～80℃，保持2～5小时，放出剩余混合浸渍液，取出木材，保存备用；步骤五，将步骤四得到的木材转移到干燥窑中，70～90℃干燥3～10天，至木材含水量为5～10％，即得到阻燃防腐木材，保存备用；步骤...
【专利技术属性】
技术研发人员：周兴安，栾涛，刘香芹，
申请(专利权)人：青岛德意佳木业有限公司，
类型：发明
国别省市：山东,37
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。