The present invention discloses a water base anti rust surface cleaning agent for flexible circuit board, which is prepared as follows: sodium alkyl sulfonate 1~5%; ether solvent 10~20%; non ionic surfactant 0.05~0.5%; EDTA 1~5%; rust inhibitor 0.2~0.6%; copper corrosion inhibitor 0.2~0.6%; preservative 0.2~2%; ketone solvent 10~20%; deionized water. Remainder. The invention provides a water base anti rust surface cleaning agent for the flexible circuit board, which is innoxious, pure and easy to handle, and does not cause damage to electrical components; it can remove some polar bromine salt, and can remove the dissolving of rosin and so on. After testing, the cleaning agent has no residue after cleaning. No white point, no other polar pollutants such as bromine salt, cleaning cleanliness of more than 96%, far exceeding the national standard of 90%.
【技术实现步骤摘要】
一种挠性线路板的水基抗锈化的表面清洗剂
本专利技术涉及化学除污领域，尤其涉及一种挠性线路板的水基抗锈化的表面清洗剂。
技术介绍
线路板清洗是利用清洗剂置入在超声波的容体中对其表面进行物理-化学处理的一项技术。根据线路板印制生产过程，一般包括如下三类残留物：一类是颗粒性污染物，如灰尘、棉绒及焊锡球。尤其地，焊锡球是一种焊接缺陷，如果设备的震动使大量小焊锡球聚集到一个部位上，便可能引起电短路。二类是非极性污染物，如助焊剂，松香、有机树脂、有机酸、有机盐及石蜡等；三类是极性沾污物，包括卤化物、及其形成的酸和盐等。上述污染物如未被清理掉，会给线路板带来如下问题：1、粉尘等易造成电路接触不良，长久聚集会被激活而带有静电，使用时易进一步吸收空气中颗粒物及粉尘；2、颗粒、锡球及极性污物形成介质会击穿电容、线路电短路、甚至于部分晶振元件会造成电性腐蚀。现有技术的线路板清洗剂清洗效果差，较多的极性污染物无法得到清理，而且使用苯、甲苯等有毒性、易挥发性、致癌性溶剂对环境及人体健康造成影响。综上所述，线路板的清洗剂凸显重要，提供一种清洗效果好，对人体健康友好的清洗剂是当前该
技术...
【技术保护点】
一种挠性线路板的水基抗锈化的表面清洗剂，其特征在于，按质量百分比配制如下：烷基磺酸钠 1~5%醚类溶剂 10~30%非离子表面活性剂 0.05~0.5%EDTA 1~5%防锈剂 0.2~0.6%铜缓蚀剂 0.2~0.6%防腐剂 0.2~2%酮类溶剂 10~30%去离子水 余量。
【技术特征摘要】
1.一种挠性线路板的水基抗锈化的表面清洗剂，其特征在于，按质量百分比配制如下：烷基磺酸钠1~5%醚类溶剂10~30%非离子表面活性剂0.05~0.5%EDTA1~5%防锈剂0.2~0.6%铜缓蚀剂0.2~0.6%防腐剂0.2~2%酮类溶剂10~30%去离子水余量。2.如权利要求1所述的一种挠性线路板的水基抗锈化的表面清洗剂，其特征在于，所述烷基磺酸钠中烷基的碳个数选自C8~C22中的一种。3.如权利要求2所述的一种挠性线路板的水基抗锈化的表面清洗剂，其特征在于，所述醚类溶剂选自乙二醇乙醚，乙二醇甲醚，丙二醇乙醚，乙二醇丙醚，丙二醇甲醚及二乙二醇二乙醚中的一种。4.如权利要求3所述的一种挠性...