This application provides a solvent based epoxy antirust primer for oil tank, its preparation and application. The primer's components include: bisphenol F liquid epoxy resin 20, 2 glass fiber 2, 5 glass fiber, 5 nano silica 5, 10 mica powder 5, 40 curing agent 55, and antifoaming 1 3. Parts, dispersants 2, 4, levelling agent 2, 4, silane coupling agent 0.5, 3, film Builder 3, 10 and solvent 10 10 20. This application provides a solvent based epoxy antirust primer for oil tanks, its preparation and application, adding glass fiber, nano silica and mica powder to improve the densification of the primer film, thus improving the corrosion resistance and antirust properties of the primer, and increasing the stability and adhesion of the anticorrosive paint used in the oil tank.
【技术实现步骤摘要】
一种石油罐用溶剂型环氧树脂防锈底漆、制备方法及应用
本申请涉及涂料
，尤其涉及一种石油罐用溶剂型环氧树脂防锈底漆、其制备方法及应用。
技术介绍
石油，又称原油，是一种粘稠的、深褐色液体地壳上层部分地区有石油储存。主要成分是各种烷烃、环烷烃、芳香烃的混合物，此外还包含硫、氧、氮、磷、钒等元素。用石油制作的燃油和汽油成为世界上最主要的能源之一，同时石油还是许多化工产品的原料。如此，石油的储存在石油的使用运输过程中尤为重要。石油罐是石油最主要的储存容器之一，现有的石油罐大多是钢铁等金属油罐。含有硫化氢、有机和无机盐以及水等腐蚀性化学物质，会造成油品贮罐发生腐蚀，腐蚀缩短了油罐的使用寿命，如果不能对金属油罐进行及时的防腐处理，也会对油品造成污染，影响油品质量；重则因腐蚀使油罐穿孔造成油品泄漏，而且容易造成火灾、爆炸，其危险性可想而知。目前，石油罐防腐多是采用：喷金属、阴极保护、防腐油漆等技术。其中防腐油漆最为广泛，常用的防腐油漆主要富锌防腐油漆，但锌防腐油漆润湿性低，附着力低，且锌粉添加到涂料中，锌粉与无机硅酸盐融合的稳定性不足。
技术实现思路
本申请提供一种石油罐用溶...
【技术保护点】
一种石油罐用溶剂型环氧树脂防锈底漆，其特征在于，所述底漆的组份按照重量分数包括：双酚F型液态环氧树脂20‑35份、玻璃纤维2‑5份、纳米二氧化硅5‑10份、云母粉5‑10份、固化剂40‑55份、消泡剂1‑3份、分散剂2‑4份、流平剂2‑4份，硅烷偶联剂0.5‑3份、成膜助剂3‑10份和溶剂10‑20份。
【技术特征摘要】
1.一种石油罐用溶剂型环氧树脂防锈底漆，其特征在于，所述底漆的组份按照重量分数包括：双酚F型液态环氧树脂20-35份、玻璃纤维2-5份、纳米二氧化硅5-10份、云母粉5-10份、固化剂40-55份、消泡剂1-3份、分散剂2-4份、流平剂2-4份，硅烷偶联剂0.5-3份、成膜助剂3-10份和溶剂10-20份。2.根据权利要求1所述的石油罐用溶剂型环氧树脂防锈底漆，其特征在于，所述底漆的组份按照重量分数包括：双酚F型液态环氧树脂30份、玻璃纤维5份、纳米二氧化硅8份、云母粉10份、固化剂45份、消泡剂2份、分散剂4份、流平剂3份，硅烷偶联剂2份、成膜助剂8份和溶剂15份。3.根据权利要求1或2所述的石油罐用溶剂型环氧树脂防锈底漆，其特征在于，所述固化剂包括聚酰胺树脂和/或改性胺树脂。4.根据权利要求1或2所述的石油罐用溶剂型环氧树脂防锈底漆，其特征在于，所述溶剂包括酯类溶剂或醇类溶剂。5.根据权利要求1或2所述的石油罐用溶剂型环氧树脂防锈...
【专利技术属性】
技术研发人员：刘骏，陈威，匡成杰，杨针玉，黄武，姚昌红，
申请(专利权)人：湖南太子化工涂料有限公司，
类型：发明
国别省市：湖南,43