The invention discloses a high antibacterial and low VOC polypropylene material and its preparation method. By mixing polypropylene particles with nanoscale alumina and / or anatase nano titanium dioxide in a high speed mixer and then pouring the blends into a twin screw extruder, the extruded strip blends are cooled after circulating water. The pellets were cut into grains and irradiated with ultraviolet light source to obtain the high antibacterial low VOC polypropylene material. The invention uses nanoscale alumina and anatase nano titanium dioxide to improve the long effect antibacterial properties of polypropylene, and reduces the VOC content of polypropylene, making the polypropylene more consistent with the green environment and expanding its application in the automotive field.
【技术实现步骤摘要】
一种高抗菌低VOC聚丙烯材料及其制备方法
本专利技术涉及工程塑料改性加工
，具体地是涉及一种高抗菌低VOC聚丙烯材料及其制备方法。
技术介绍
塑料在满足汽车美观、舒适、安全、防腐、轻量化及设计自由度大等方面起着其它材料无法替代的作用。近年来，塑料在汽车上的应用获得了巨大的发展，其应用领域已扩展到整车的各大总成系统。聚丙烯材料以其来源广泛、密度小、力学均衡性好、耐化学腐蚀、易加工及价格低廉等突出优点，使其成为了汽车领域使用量最大的塑料，加之其优异的性能价格比，使各种增韧、填充、增强聚丙烯材料在汽车各大总成系统中获得了广泛应用。随着汽车工业的发展，节能和环保逐渐成为了汽车工业的两大课题，人们对健康和环保的认识与要求也不断提高。聚丙烯塑料在使用和存放过程中，在适宜的温度和湿度条件下，制品表面会大量滋生对人体健康有害的细菌等微生物，然而聚丙烯本身并没有抗菌特性，同时聚丙烯树脂中残留的过氧化物以及与基体相溶性较差的加工助剂都会产生VOC，对人体的身心健康有很大潜在伤害，这都极大限制了聚丙烯在汽车领域的应用。纳米TiO2作为一种非常重要的无机功能材料主要有两种结晶形态：...
【技术保护点】
一种高抗菌低VOC聚丙烯材料的制备方法，其特征在于包括以下步骤：步骤1，按质量份数计，将100份聚丙烯颗粒和0.5份‑5份的纳米级氧化铝和/或锐钛型纳米二氧化钛倒入高速混炼机中搅拌共混，得到共混物；步骤2，将步骤1得到的共混物倒入双螺杆挤出机进行挤出造粒，挤出的条状共混物经过循环水冷却后进入切粒机切粒，得到粒料；步骤3，将步骤2得到的粒料经过紫外光源辐照，即可得到所述高抗菌低VOC聚丙烯材料。
【技术特征摘要】
1.一种高抗菌低VOC聚丙烯材料的制备方法，其特征在于包括以下步骤：步骤1，按质量份数计，将100份聚丙烯颗粒和0.5份-5份的纳米级氧化铝和/或锐钛型纳米二氧化钛倒入高速混炼机中搅拌共混，得到共混物；步骤2，将步骤1得到的共混物倒入双螺杆挤出机进行挤出造粒，挤出的条状共混物经过循环水冷却后进入切粒机切粒，得到粒料；步骤3，将步骤2得到的粒料经过紫外光源辐照，即可得到所述高抗菌低VOC聚丙烯材料。2.如权利要求1所述的一种高抗菌低VOC聚丙烯材料的制备方法，其特征在于：所述步骤1中，所述高速混炼机的搅拌速度设置在400转/分钟-450转/分钟，共混时间为10分钟-15分钟。3.如权利要求1所述的一种高抗...
【专利技术属性】
技术研发人员：李庆蛟，吴斌，郁胜振，李文波，
申请(专利权)人：苏州银禧科技有限公司，
类型：发明
国别省市：江苏,32