The invention provides a preparation process for the processing aids for the PVC substrate. In the reactor, acetacetone, stearic acid and Zinc Oxide are added to the reactor, the stirring heating is heated to 110 ~140 C, and the target product is obtained after adding a certain amount of catalyst to react to 40min. The composite of zinc acetylacetonate and zinc stearate yield 94~96.0%, zinc content 20%~24%, melting point 129 ~133 C. The lubricant dispersing effect of the product obtained by adopting the technological conditions of the invention is relatively ideal, and has good dispersibility and aging resistance.
【技术实现步骤摘要】
一种PVC基材色母用加工助剂的制备工艺
本专利技术涉及化学助剂领域，具体涉及一种PVC基材色母用加工助剂的制备工艺，制备的产品乙酰丙酮锌与硬脂酸锌的复合物应用在PVC色母加工。
技术介绍
PVC制品目前90%以上使用色粉进行调色，但存在问题是色粉的预分散处理容易造成色粉的团聚，在PVC制品加工成型过程中，色粉的团聚对制品颜色的均匀性染色差，易出现花纹线，影响制品外观和产品的理学性能。色母是将颜料与树脂进行充分分散混合后的高度浓缩的颜料添加剂产品，基于极性相似相容原理，色母所用树脂与塑料加工所用树脂一般为同类型。保证了在塑料成型过程中，色母替代色粉添加到制品配方中能有效解决色粉分散不良造成制品缺陷的问题。在PVC加工中使用的色母大多数是EVA和PE塑料为基材的色母，该类色母存在着基材与PVC制品相容性的问题，所以添加量受到很大限制。而由于PVC树脂本身耐热性能差，对加工助剂依赖度高导致目前市面上很少见到以PVC为基材的色母。目前在助剂市场中尚未发现专门用于以PVC为基材的色母加工助剂，受限于此也未发现PVC专用色母。也无相关文献和专利提到以PVC为基材的色母加工助剂...
【技术保护点】
一种PVC基材色母用加工助剂的制备工艺，其特征在于：乙酰丙酮、硬脂酸和氧化锌混合加入反应器中，搅拌加热升温至110℃~140℃，加入一定量催化剂反应20‑50min后得到目标产品，目标产品为乙酰丙酮锌与硬脂酸锌的复合物。
【技术特征摘要】
1.一种PVC基材色母用加工助剂的制备工艺，其特征在于：乙酰丙酮、硬脂酸和氧化锌混合加入反应器中，搅拌加热升温至110℃~140℃，加入一定量催化剂反应20-50min后得到目标产品，目标产品为乙酰丙酮锌与硬脂酸锌的复合物。2.根据权利要求1所述的PVC基材色母用加工助剂的制备工艺，其特征在于：乙酰丙酮、硬脂酸、氧化锌与催化剂质量百分比分别为30~32%，48~54%，15~19.5%，0.05~0.5%，各组分的重量百分比应为100%。3.根据权利要求1所述的PVC基材色母用加工助剂的制备工艺，其特征在于：所述制备的乙酰丙酮锌与硬脂酸锌的复合物为白色，熔点为128℃~132℃。4.根据权利要求1所述...
【专利技术属性】
技术研发人员：王玉梅，胡丹，荀育军，石舒敏，陈立桓，
申请(专利权)人：东莞市汉维科技股份有限公司，
类型：发明
国别省市：广东,44