The invention provides a spelling glue emulsion for red wood and a preparation method, which belongs to the field of adhesive technology, and is prepared by using the emulsion with high stickiness, strong boiling water resistance and good weatherability. The red wood collage glue emulsion is made up of 30~35 parts of polyvinyl alcohol, 2~3 parts of sodium bicarbonate, 15~20 emulsifiers, 3~4 initiators, 40~80 methyl methacrylate, 450~500 vinyl acetate, 5~10 acrylic acid 2 hydroxyethyl ester, 4 acrylic acid 4 hydroxybutyl 10~15, 1~2 copies of acrylic acid, 3~5 organic siloxane, 0.5 to 1 phr twelve alkyl mercaptan, 0.5 to 1 Sodium Bisulfite, 0.5 to 1 defoamer, 2~3 antiseptic and 450~500 deionized water. The mahogany board adhesive emulsion is used for preparing the glue board, which can be effectively used for the red wood splicing process.
【技术实现步骤摘要】
一种红木用拼板胶乳液及其制备方法
本专利技术属于胶黏剂
，尤其涉及一种红木用拼板胶中使用的乳液及其制备方法。
技术介绍
我国是世界上木材及木制品的生产和消费大国，同时也是人均占有森林资源最少的国家，木材的供需矛盾非常尖锐。拼板胶作为一种木材胶粘剂，能够将木材加工剩余物和短小级木材拼接成大面积的集成材，对于木材的有效利用起着很重要的作用。红木特指紫檀木、花梨木、黑酸枝、红酸枝、鸡翅木等珍贵木材，木质硬重、强度高，拼接难度大。传统的“三醛”胶粘剂、聚醋酸乙烯酯胶粘剂胶层较脆，粘接后容易开裂，耐沸水煮能力、耐候性差。
技术实现思路
本专利技术提供了一种红木用拼板胶乳液及其制备方法，该乳液用于制备拼板胶，使其粘接牢度高，耐沸水煮能力强，耐候性好，可有效用于红木拼接。为了达到上述目的，本专利技术提供了一种红木用拼板胶乳液，各组份及其重量份数组成为：在上述技术方案中，添加有机硅氧烷作为交联单体，有机硅氧烷含有甲基丙烯酰氧基有机基和甲氧基硅烷基无机基的双官能团，同时具备有机反应性与无机反应性，有机/无机界面处可以与有机基硅烷发生化学键结，从而提高粘结强度。另外，配方中还添加有...
【技术保护点】
一种红木用拼板胶乳液，其特征在于，各组份及其重量份数组成为：
【技术特征摘要】
1.一种红木用拼板胶乳液，其特征在于，各组份及其重量份数组成为：2.根据权利要求1所述的红木用拼板胶乳液，其特征在于，所述聚乙烯醇为PVA1788、PVA0588、PVA1792或PVA1799中的一种或两种以上按任意配比组成的混合物。3.根据权利要求1所述的红木用拼板胶乳液，其特征在于，所述乳化剂为烷基硫酸盐、硫基琥珀酸聚氧乙烯醚酯或脂肪醇聚氧乙烯醚中的一种或两种以上按任意配比组成的混合物。4.根据权利要求1所述的红木用拼板胶乳液，其特征在于，所述引发剂为过硫酸钾、过硫酸钠或过硫酸铵中的一种。5.根据权利要求1所述的红木用拼板胶乳液，其特征在于，所述有机硅氧烷为γ-甲基丙烯酰氧基丙基三甲氧基硅烷。6.根据权利要求1所述的红木用拼板胶乳液，其特征在于，所述消泡剂为聚二甲基硅氧烷。7.根据权利要求1所述的红木用拼板胶乳液，其特征在于，所述防腐剂为苯甲酸钠。8.一种如权利要求1-7任一项所述的红木用拼板胶乳液的制备方法，其特征在于，包括以下步骤：1)将0.8～1.2份引发剂溶解于5～10份去离子水中，得初引发剂；将2～2.5份引发剂溶解于40～5...
【专利技术属性】
技术研发人员：郑军，张士军，刘毅，
申请(专利权)人：保定光普化工研究所，
类型：发明
国别省市：河北,13