中和剂在控制EVA弹性体乳液的乳液粒径中的应用制造技术
Application of neutralizer in controlling the particle size of EVA elastomer emulsion
The present invention relates to a neutralizing agent in the control of EVA elastomer emulsion particle size in the application, including: in a single reactor, with deionized water as the aqueous phase, emulsifier and vinyl acetate, then adding neutralizing agent, vinyl acetate and ethylene under the action of initiator for polymerization, obtained EVA elastic emulsion. According to the invention, the neutralizer can control the particle size of the emulsion, reduce the particle size of the emulsion, prevent the adhesion and improve the stability and dispersity of the system.
【技术实现步骤摘要】
中和剂在控制EVA弹性体乳液的乳液粒径中的应用
本专利技术涉及一种EVA弹性体领域，具体涉及中和剂在控制EVA弹性体微乳液粒径中的应用。
技术介绍
乳液聚合法生产的EVA(乙烯/乙酸乙烯酯共聚物)弹性体乳液，乙酸乙烯酯(VAc)含量适中，产品具有优良的柔韧性、透明性、低温挠曲性、耐候性、耐化学药品腐蚀性及与填料和色母料的相容性；EVA乳液产品强度高、无毒环保、粘结性能优异，可用于纺织、轻工、涂料、塑料增韧、建筑用配制料、聚合物掺混涂层，橡胶改性等领域，应用广泛，其国内外需求量不断增加，近年来发展迅速。专利CN1302027C在40-60℃引发聚合制备高固体EVA胶乳，反应乙烯计重不计压力，引发剂用量0.01-3.0wt％，反应时间10.0h。聚合物中VAc含量75.0-99.0wt％。由于形成了乳液和悬浮液聚合物，所以得到的分散体具有双峰粒度分布，例如最大值在0.2-0.5μm和在3.0-6.0μm的峰。专利CN101200518A采用双氧水-硫酸亚铁体系，70-75、75-80℃两阶段阶梯控温引发聚合，乙烯反应压力9.0-10.0MPa，粒子直径1.85μm。以...
【技术保护点】
中和剂在控制EVA弹性体乳液的乳液粒径中的应用，包括：于单个反应器中，以去离子水为水相，依次加入乳化剂和乙酸乙烯酯，然后加入中和剂，在胶体保护剂的存在下，乙酸乙烯酯和乙烯在引发剂的作用下进行共聚合反应，得到EVA弹性体乳液。
【技术特征摘要】
1.中和剂在控制EVA弹性体乳液的乳液粒径中的应用，包括：于单个反应器中，以去离子水为水相，依次加入乳化剂和乙酸乙烯酯，然后加入中和剂，在胶体保护剂的存在下，乙酸乙烯酯和乙烯在引发剂的作用下进行共聚合反应，得到EVA弹性体乳液。2.根据权利要求1所述的应用，其特征在于，所述中和剂选自氢氧化钠、氢氧化钾、碳酸氢钠、醋酸钠、焦磷酸钠、碳酸钠和氨水中的一种或多种，优选所述中和剂的用量为乙酸乙烯酯用量的0.1-7.0wt％，更优选0.2-6.0wt％。3.根据权利要求2所述的应用，其特征在于，所述乳化剂为非离子表面活性剂，优选所述非离子表面活性剂选自烷基酚聚氧乙烯醚、脂肪醇聚氧乙烯醚和脂肪酸甲酯聚氧乙烯醚，更优选所述非离子表面活性剂的用量为乙酸乙烯酯用量的0.05-20.0wt％，优选5.0-15.0wt％。4.根据权利要求1-3中任意一项所述的应用，其特征在于，所述引发剂选用水溶性自由基引发剂，优选自无机盐、偶氮化合物、无机过氧化物以及无机氧化还原引发剂中的一种或几种，更优选选自过硫酸铵、过硫酸钠、过硫酸钾、偶氮二异丁咪唑啉盐酸盐、偶氮二氰基戊酸、偶氮二异丁基脒盐酸盐、双氧水和过氧化钠中一种或几种；其中，优选所述引发剂的用量为乙酸乙烯酯用...
【专利技术属性】
技术研发人员：陈博，刘小萌，于鲁强，刘金伟，
申请(专利权)人：中国石油化工股份有限公司，中国石油化工股份有限公司北京化工研究院，
类型：发明
国别省市：北京,11