The invention provides a water-based sealant emulsion and a preparation method, which belongs to the field of adhesive technology. The water sealant prepared by the emulsion has high bond strength, good heat resistance and good frost resistance. The water sealant glue emulsion and its weight share are: 15~20 polyvinyl alcohol, 2~3 sodium bicarbonate, 15~20 emulsifiers, 3~4 initiators, 300~500 butyl acrylate, 100~300 vinyl acetate, 10~20 acrylic acid 2 hydroxyethyl ester, 1~2 acroleic acid, 1~2 portion of acrylic acid, and twelve alkyl mercaptan. Sodium Bisulfite has 0.5 to 1 parts, 0.5 to 1 defoamer, 2~3 antiseptic and 450~500 deionized water. The water-based sealant emulsion provided by the invention is used for the preparation of water-based sealant, which can be effectively used for BOPP/ paper, polishing / paper, PET/ paper, paper / paper, ink / paper, and UV / paper sealing or opening.
【技术实现步骤摘要】
一种水性封口胶乳液及其制备方法
本专利技术属于胶黏剂
，尤其涉及一种水性封口胶中使用的乳液及其制备方法。
技术介绍
封口胶是包装工业中使用较为广泛的一种胶粘剂，用于纸盒、纸箱和手提袋等的封边接口。封口胶主要有油性封口胶和水性封口胶两种。油性封口胶一般以甲苯等为溶剂，以SBS、萜烯树脂和松香等为主要原料，对环境和身体健康都有较大危害。水性封口胶是以水为分散介质的环保型胶粘剂，无毒害、无污染，正在逐渐取代油性封口胶。市场上现有的很多水性封口胶在使用后，制成的包装品在高温或低温环境下容易脱胶，给企业造成损失，原因在于这些水性封口胶的粘结强度、耐高温和耐低温性能较差。
技术实现思路
本专利技术提供了一种水性封口胶乳液及其制备方法，使用该乳液制备的水性封口胶耐热性好，抗冻性佳，可有效用于BOPP/纸、磨光/纸、PET/纸、纸/纸、油墨/纸和UV上光/纸的封边或搭口。为了达到上述目的，本专利技术提供了一种水性封口胶乳液，各组份及其重量份数组成为：在上述技术方案中，选用丙烯酸丁酯作为软单体、醋酸乙烯作为硬单体，二者共聚后能产生较好的内聚强度，提高耐水性、附着力和透明性。选用丙...
【技术保护点】
一种水性封口胶乳液，其特征在于，各组份及其重量份数组成为：
【技术特征摘要】
1.一种水性封口胶乳液，其特征在于，各组份及其重量份数组成为：2.根据权利要求1所述的水性封口胶乳液，其特征在于，所述聚乙烯醇为PVA1788、PVA0588、PVA1792或PVA1799中的一种或两种以上按任意配比组成的混合物。3.根据权利要求1所述的水性封口胶乳液，其特征在于，所述乳化剂为烷基硫酸盐、硫基琥珀酸聚氧乙烯醚酯或脂肪醇聚氧乙烯醚中的一种或两种以上按任意配比组成的混合物。4.根据权利要求1所述的水性封口胶乳液，其特征在于，所述引发剂为过硫酸钾、过硫酸钠或过硫酸铵中的一种。5.根据权利要求1所述的水性封口胶乳液，其特征在于，所述消泡剂为聚二甲基硅氧烷。6.根据权利要求1所述的水性封口胶乳液，其特征在于，所述防腐剂为苯甲酸钠。7.一种如权利要求1-6任一项所述的水性封口胶乳液的制备方法，其特征在于，包括以下步骤：1)将0.4～0.6份引发剂溶解于5～10份水中，得初引发剂；将2.5～3.1份引发剂...
【专利技术属性】
技术研发人员：郑军，刘毅，张士军，
申请(专利权)人：保定光普化工研究所，
类型：发明
国别省市：河北,13