锌掺杂523三元材料前驱体的制备方法技术
Preparation method of zinc doped 523 three element precursor
The invention relates to a preparation method of a lithium ion battery cathode material precursor, in particular to a preparation method of a zinc doped 523 three yuan material precursor. The battery grade NiSO4 solution, CaSO4 solution and MnSO4 solution are mixed to the mixed solution, and the ammonia water is added to adjust the pH, then Na2CO3 solution and zinc salt are added to the salt solution. After the reaction, it is statically washed, filtered and dried, and the zinc doped 523 three yuan material precursor is obtained. The invention has the advantages of short process and low cost, and has prepared zinc doped 523 three yuan material precursor, which has high density of compaction and is used for the assembly and preparation of lithium ion batteries.
【技术实现步骤摘要】
锌掺杂523三元材料前驱体的制备方法
本专利技术涉及一种锂离子电池正极材料前驱体的制备方法，具体涉及一种锌掺杂523三元材料前驱体的制备方法。
技术介绍
镍钴锰酸锂为一种新型锂离子二次电池正极材料，具有放电容量高，循环性能好成本低廉，无污染，安全性高等优点。具有广阔的应用前景，该材料已广泛的应用在锂离子电池上。而镍钴锰三元素复合氢氧化物是生产锂离子电池正极材料的重要中间体，其指标对锂离子电池物理性能和电化学性能有着重要的影响。因此开发高性能三元前驱体是生产动力电池以及其它高端电池用正极材料的基础。在制备523三元前驱体过程中，由于Ni，Co，Mn离子的粒径大小不同，制备的前驱体离子间存间隙，使得振实密度较小，同时形貌均匀性较差。通过Zn改性，Zn粒镶嵌在粒子之间，增加了前驱体的振实密度，改善粒子的形貌特征。专利“F取代523三元材料的制备方法(201510072336.3)”中公开了一种F取代523三元材料的制备方法。将NH4F于玛瑙研钵中研细后，以0.5％-2％的质量比与已制备好并破碎的523三元材料在三维锥混机内混合均匀；将混合物在400-700℃进行烧结；冷...
【技术保护点】
一种锌掺杂523三元材料前驱体的制备方法，其特征在于：将电池级NiSO4溶液、CaSO4溶液和MnSO4溶液混合得到混合溶液，加入氨水调节pH，再逐滴加入Na2CO3溶液和锌盐进行溶盐反应，反应后静置，洗涤、过滤、烘干，研磨得到锌掺杂523三元材料前驱体。
【技术特征摘要】
1.一种锌掺杂523三元材料前驱体的制备方法，其特征在于：将电池级NiSO4溶液、CaSO4溶液和MnSO4溶液混合得到混合溶液，加入氨水调节pH，再逐滴加入Na2CO3溶液和锌盐进行溶盐反应，反应后静置，洗涤、过滤、烘干，研磨得到锌掺杂523三元材料前驱体。2.根据权利要求1所述的锌掺杂523三元材料前驱体的制备方法，其特征在于：混合溶液中NiSO4的浓度为1.5-3mol，Ni离子：Co离子：Mn离子的摩尔比为5:2:3。3.根据权利要求1所述的锌掺杂523三元材料前驱体的制备方法，其特征在于：加入氨水调节pH至7-9。4.根据权利要求1所述的锌掺杂523三元材料前驱体的制备方法，其特征在于：所述的锌盐...
【专利技术属性】
技术研发人员：张亚莉，楚玮，
申请(专利权)人：淄博国利新电源科技有限公司，
类型：发明
国别省市：山东,37