The invention relates to the field of water reducing agent, in particular to an efficient environmental water reducing agent and its preparation method. The water reducing agent is made of the following weight raw materials: Cotton Cellulose 20, 30, 10, 15, 10, 20, soluble starch 5, 10, 7 sodium hychlorinate, 1 ethylene oxide, 5 portion of epoxy ethane. Ammonium sulfate 1, 4 lithium carbonate, 2 lithium carbonate 5 copies, 0.5 sulfonyl methyl phenol formaldehyde resin 1.5, 0.5 fulvic acid 1, water right amount; the water reducing agent provided by the invention effectively compensates for the existing water reducing agent in poor durability, poor impermeability, and limited water reducing effect.
【技术实现步骤摘要】
一种高效环保减水剂及其制备方法
本专利技术涉及减水剂领域，具体涉及一种高效环保减水剂及其制备方法。
技术介绍
减水剂是一种在维持混凝土坍落度不变的条件下，能减少拌合用水量的混凝土外加剂。大多属于阴离子表面活性剂，有木质素磺酸盐、萘磺酸盐甲醛聚合物等。加入混凝土拌合物后对水泥颗粒有分散作用，能改善其工作性，减少单位用水量，改善混凝土拌合物的耐久性；或减少单位水泥用量，节约水泥。在中国公开的专利申请CN104119021B中针对获得一种高效环保减水剂，其由以下重量份的原料混合而成：β-萘磺酸盐甲醛缩合物50-60、聚乙二醇单甲醚甲基丙烯酸酯20-30、木质素磺酸钙15-25、环氧乙烷-环氧丙烷共聚物10-15、海藻糖2-4、硅酮粉1.5-2.5、页岩灰4-8、亚硫酸氢钠2.5-4.5、聚氧化乙烯5-10、三聚磷酸铝8-14、椰油酰二乙醇胺2-3、二壬基萘磺酸钡1-2、乌洛托品2-3、助剂3-5。本专利技术减水剂减水率高、耐久性好，可明显改善混凝土耐久性和工作度，终凝后早强效果显著，能大幅度提高混凝土各龄期的强度，适用于各类混凝土；在中国公开的专利申请CN1019482...
【技术保护点】
一种高效环保减水剂，该减水剂由如下重量份原料制成：棉纤维素20‑30份、异丙醇10‑15份、1,4‑丁基磺酸内酯10‑20份、可溶性淀粉5‑10份、次氯酸钠2‑7份、环氧乙烷1‑5份、过硫酸铵1‑4份、碳酸锂2‑5份、磺甲基酚醛树脂0.5‑1.5份、黄腐酸0.5‑1份、水适量。
【技术特征摘要】
1.一种高效环保减水剂，该减水剂由如下重量份原料制成：棉纤维素20-30份、异丙醇10-15份、1,4-丁基磺酸内酯10-20份、可溶性淀粉5-10份、次氯酸钠2-7份、环氧乙烷1-5份、过硫酸铵1-4份、碳酸锂2-5份、磺甲基酚醛树脂0.5-1.5份、黄腐酸0.5-1份、水适量。2.根据权利要求1所述的高效环保减水剂，其特征在于，该减水剂由如下重量份原料制成：棉纤维素25-28份、异丙醇11-14份、1,4-丁基磺酸内酯11-15份、可溶性淀粉6-8份、次氯酸钠3-5份、环氧乙烷2-4份、过硫酸铵2-3份、碳酸锂3-4份、磺甲基酚醛树脂0.6-1份、黄腐酸0.6-0.8份、水适量。3.根据权利要求1所述的高效环保减水剂，其特征在于，该减水剂的制备方法包括如下几个步骤：(1)将棉纤维素和异丙醇加入反应锅内，加入与棉纤维素质量相等的水，搅拌均匀后，加入五分之一于棉纤维素的30％氢氧化钠水溶液碱化一段时间；(2)将步骤(1)中反应锅至于75-80℃的恒温水浴箱中，冲入氮气，并在一定转速的机械搅拌的条件下滴加1,4-丁基磺酸内酯，反应2-3...
【专利技术属性】
技术研发人员：马丽涛，崔岩，王硕，
申请(专利权)人：萧县沃德化工科技有限公司，
类型：发明
国别省市：安徽,34