The invention relates to the field of PVC drainage pipe, and the lead free PVC drainage pipe and its preparation method are made, which consist of the following weight components: PVC resin 90, 110 copies, compound calcium zinc heat stabilizer 5, 15 CaCO35, 9 CPE7, 2 MBS1, 4 titanium dioxide, 0.01 PE wax 0.01, 0.2, Zinc Oxide whisker 5 15, nanoscale. 1 zinc powders, 1 nanoscale clay 10, 0.1 ultraviolet absorbents 1, 0.1 antioxidants 1 and 0.1 stearic acids, including calcium stearate and zinc stearate, the mass ratio of calcium stearate and zinc stearate is 4.1:1 5:1. The lead-free PVC drainpipe obtained by the invention has the functions of bacteriostasis, retarding aging and the like, and is nontoxic and environmentally friendly. By adjusting the technological parameters, the color difference of the drainage pipe is improved.
【技术实现步骤摘要】
无铅PVC排水管及其制备方法
本专利技术涉及排水管领域，尤其涉及了无铅PVC排水管及其制备方法。
技术介绍
聚氯乙烯(PVC)是最常见的树脂之一，是世界上实现工业化时间最早、应用范围最广的通用型热塑性塑料。PVC结构不稳定，在加工成型中容易降解：当加工温度达到90℃时，就会发生轻微的热分解反应；当温度达到120℃时，会发生明显的热分解反应，使PVC的颜色逐渐加深。因此，在PVC在加工过程中，必须使用热稳定剂，以防止其热分解。常用的热稳定剂主要有铅盐类、金属皂类、有机锡类、稀土类和钙锌类等稳定剂。随着人们环保意识的进一步增强，铅盐类的使用量正逐渐减少；而有机锡类由于其价格原因，得不到广泛的推广。钙锌热稳定剂是目前世界上公认的无毒、环保型热稳定剂，且价格低廉、润滑性良好等，因此具有极广阔的发展空间。排水管常用于雨水、污水、农田排灌等排水的任务，容易引起某些微生物繁殖，包括细菌、真菌、酵母菌、藻类及病毒等。因此需要添加具有抗菌性能的物质，使微生物的生长或繁殖保持在一定的范围内。
技术实现思路
本专利技术针对现有技术的缺点，提供了一种具有抑菌、延缓老化等功能的无毒、环保的无铅...
【技术保护点】
无铅PVC排水管，其特征在于，由以下重量份的成分组成：
【技术特征摘要】
1.无铅PVC排水管，其特征在于，由以下重量份的成分组成：复合钙锌热稳定剂由硬脂酸钙和硬脂酸锌组成，硬脂酸钙和硬脂酸锌的质量比为4.1:1～5:1。2.根据权利要求1所述的无铅PVC排水管，其特征在于：硬脂酸钙和硬脂酸锌的质量比为4.5:1。3.根据权利要求1所述的无铅PVC排水管，其特征在于，由以下重量份的成分组成：4.一种根据权利要求1所述的无铅PVC排水管的制备方法，其特征在于，包括如下步骤：(1)将纳米锌粉末通过离子吸附法固定在纳米粘土上，得到粉末；(2)原料混合：按所述配比取PVC树脂、硬脂酸钙、硬脂酸锌、CaCO3、氧化锌晶须、CPE、MBS、钛白粉、PE蜡、紫外线吸收剂、抗氧化剂、硬脂酸和步骤(1)得到的粉末在高速混料机中混合，得到混合料；(3)造粒：步骤(1)中的混合料利用双螺杆挤出机造粒，双螺杆挤出机的筒区温度采取抛物线设置，得到PVC粒子；(4)挤出成...
【专利技术属性】
技术研发人员：严春强，潘刚，金晓松，方林，黄英巧，
申请(专利权)人：浙江高峰控股集团有限公司，
类型：发明
国别省市：浙江,33
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。