The invention relates to a preparation method of anti-aging agents, which belongs to the field of chemical preparation. Its characteristics are: take TiO2 (KH - 560) powder, deionized water, stir in three bottles, and then put into ultrasonic apparatus and ultrasonic treatment; take water bath and add LAS and AN; heat up to the reaction temperature to add initiator; after the reaction ends, PAN and unreacted AN with N, N - two methyl formamide and acetone; clean clean. The product is dried in a vacuum drying box, and then the aging agent product is prepared. By improving the process and adjusting the amount of the reactant in the preparation process, the properties of the prepared aging agent are improved, the grafting ratio is greatly improved, the performance is stable, and the preparation process is simple, and it is suitable for industrial production.
【技术实现步骤摘要】
一种抗老化剂的制备方法
本专利技术属于化学制备领域，尤其涉及一种抗老化剂的制备方法。
技术介绍
在现代生活中，各种化学制剂已深入到生活的各个方面，吃穿住行各行业都有化学制剂的存在，给人们的生活带来极大的便利，但同时给人们的健康与环境的治理带来了诸多问题。近年来，随着科技的快速进步，各种有机可分解且环保的化学制剂被开发并利用起来，聚丙烯(PP)具有结晶度高、结构规整、耐热性好、化学稳定性好等特点而被广泛应用，但是其抗紫外性能差、与无机物的相容性差，导致它在一些应用上受到了限制。
技术实现思路
本专利技术旨在解决上述问题，提供一种抗老化剂的制备方法。一种抗老化剂的制备方法，其特征在于：取TiO2(KH–560)粉末1g，量取50mL的去离子水，放入250mL的三口瓶内搅拌30min，然后放入超声器内超声处理；进行水浴并加入LAS和AN；升温到反应温度后加入引发剂；待反应结束后，用N，N–二甲基甲酰胺和丙酮反复洗去反应中易产生的PAN和未反应的AN副产物；将清洗干净的产物放到真空干燥箱内干燥，便得到TiO2(KH–560)-g-AN产物。本专利技术所述的一种抗老化剂的制备方...
【技术保护点】
一种抗老化剂的制备方法，其特征在于：取TiO2(KH–560)粉末1g，量取50mL的去离子水，放入250mL 的三口瓶内搅拌30min，然后放入超声器内超声处理；进行水浴并加入LAS和AN；升温到反应温度后加入引发剂；待反应结束后，用N，N–二甲基甲酰胺和丙酮反复洗去反应中易产生的PAN和未反应的AN副产物；将清洗干净的产物放到真空干燥箱内干燥，便得到TiO2(KH–560)‑g‑AN产物。
【技术特征摘要】
1.一种抗老化剂的制备方法，其特征在于：取TiO2(KH–560)粉末1g，量取50mL的去离子水，放入250mL的三口瓶内搅拌30min，然后放入超声器内超声处理；进行水浴并加入LAS和AN；升温到反应温度后加入引发剂；待反应结束后，用N，N–二甲基甲酰胺和丙酮反复洗去反应中易产生的PAN和未反应的AN副产物；将清洗干净的产物放到真空干燥箱内干燥，便得到TiO2(KH–560)-g-AN产物。2.如权利要求1所述的一种抗老化剂的制备方法，其特征在于所述引发剂为KPS。3.如权利要...
【专利技术属性】
技术研发人员：王耀斌，
申请(专利权)人：陕西盛迈石油有限公司，
类型：发明
国别省市：陕西,61
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。