一种陶粒砼轻质墙板及制备制造技术

一种陶粒砼轻质墙板及制备，其特点是：其组成成分为陶粒、水泥、矿渣、防水剂、减水剂、防冻剂；其成分比例为（重量计）陶粒58‑75%、水泥13‑21%、矿渣11‑21%、防水剂0.13‑0.92%、减水剂0.098‑0.69%、防冻剂0.065‑1.15%。它解决了目前在建筑中非承重外墙广泛使用的加汽水泥砖、炉渣粉煤灰砖、粉煤灰石子水泥砖等存在的吸水率高、粘贴瓷砖石材易开裂脱落、整体结构强度低，抗冲击、抗弯折荷载低等问题，适应于在建筑中使用。

A lightweight ceramsite concrete wallboard and its preparation

A lightweight ceramsite concrete wall panel and its preparation, characterized by its components are ceramsite, cement, slag, waterproofing agent, water reducer and antifreeze; its composition ratio is (weight meter) 58 clay 75%, cement 13 21%, slag 11 21%, waterproofing agent 0.13 0.92%, water reducer 0.098 0.69%, antifreeze 0.065 1.15% 1.15%. It solves the problems of high water absorption rate, easy cracking and falling off, low overall structure strength, low impact and low bending load, and so on, which should be used in the building.

【技术实现步骤摘要】
一种陶粒砼轻质墙板及制备
本专利技术涉及建材领域，具体的说是一种以陶粒作为骨料、矿渣为辅料的砼轻质外墙板。
技术介绍
目前，在建筑中广泛使用的非承重外墙主要有加汽水泥砖、炉渣粉煤灰砖、粉煤灰石子水泥砖等。加汽水泥砖吸水率高，粘贴瓷砖石材易开裂脱落，且不可以钉、钻及横、纵向穿线；炉渣粉煤灰砖、粉煤灰石子水泥砖吸水率高，易开裂，整体结构强度低，抗冲击、抗弯折荷载低。
技术实现思路
本专利技术为解决目前建筑中使用的非承重外墙砖存在的吸水率高，易开裂，易变形，抗冲击、抗弯荷载低，抗震防震效果差等问题，专利技术一种以陶粒为骨料、矿渣为辅料的陶粒砼轻质外墙板及其制备方法。本专利技术为解决上述技术问题，所采取的技术方案是，一种陶粒砼轻质墙板及制备，其特殊之处包括：1、组成成分为：陶粒、水泥、矿渣、防水剂、减水剂、防冻剂；2、成分比例为（重量计）：陶粒58-75%、水泥13-21%、矿渣11-21%、防水剂0.13-0.92%、减水剂0.098-0.69%、防冻剂0.065-1.15%。3、工艺为：（1）选料：按比例称取上述6种配料；（2）搅拌：将按比例称取的配料置于搅拌机中加水搅拌2-3分钟；（3）制本文档来自技高网...

【技术保护点】
一种陶粒砼轻质墙板及制备，其特征是成分为：陶粒、水泥、矿渣、防水剂、减水剂、防冻剂；其成分比例为（重量计）：陶粒58‑75%、水泥13‑21%、矿渣11‑21%、防水剂0.13‑0.92%、减水剂0.098‑0.69%、防冻剂0.065‑1.15%。

【技术特征摘要】
1.一种陶粒砼轻质墙板及制备，其特征是成分为：陶粒、水泥、矿渣、防水剂、减水剂、防冻剂；其成分比例为（重量计）：陶粒58-75...

【专利技术属性】
技术研发人员：刘成其，
申请(专利权)人：刘成其，
类型：发明
国别省市：山东,37