A lightweight concrete exterior wall plate, characterized by its composition of coarse ceramsite (0.5 1.0cm), medium ceramsite (0.5cm), ceramsite powder (below 0.3cm), cement, waterproofing agent, water reducer and antifreeze; its composition is (gravometer) coarse ceramsite (phi 0.5 1.0cm) 34.5, 43%, medium ceramsite (0.3). 0.5cm) 6.9 and 17.2%, ceramsite powder (below 0.3cm) 13.8 25.8%, cement 13 21%, waterproof agent 0.13 0.92%, water reducer 0.098 0.69%, antifreeze 0.065 1.15%. It solves the problems of high water absorption rate, easy cracking and falling off, low overall structure strength, low impact and low bending load, and so on, which should be used in the building.
【技术实现步骤摘要】
一种轻质混凝土外墙板
本专利技术涉及建材领域,具体的说是一种以陶粒作为骨料、陶粒粉末为辅料的混凝土轻质外墙板。
技术介绍
目前,在建筑中广泛使用的非承重外墙材料主要有加汽水泥砖、炉渣粉煤灰砖、粉煤灰石子水泥砖等。加汽水泥砖吸水率高,粘贴瓷砖石材易开裂脱落,且不可以钉、钻及横、纵向穿线;炉渣粉煤灰砖、粉煤灰石子水泥砖吸水率高,易开裂,整体结构强度低,抗冲击、抗弯折荷载低。
技术实现思路
本专利技术为解决目前建筑中使用的非承重外墙砖存在的吸水率高,易开裂,易变形,抗冲击、抗弯荷载低,抗震防震效果差等问题,专利技术一种以陶粒为骨料、陶粒粉末为辅料的陶粒混凝土轻质外墙板及其制备方法。本专利技术的技术方案是,一种轻质混凝土外墙板,其特殊之处包括:组成成分为:粗陶粒(φ0.5-1.0cm)、中陶粒(φ0.3-0.5cm)、陶粒粉末(φ0.3cm以下)、水泥、防水剂、减水剂、防冻剂;成分比例为(重量计):粗陶粒(φ0.5-1.0cm)34.5-43%、中陶粒(φ0.3-0.5cm)6.9-17.2%、陶粒粉末(φ0.3cm以下)13.8-25.8%、水泥13-21%、防水剂0.13-0.92%、减水剂0.098-0.69%、防冻剂0.065-1.15%。工艺为:(1)选料:按比例称取上述7种配料;(2)搅拌:将按比例称取的配料置于搅拌机中加水搅拌2-3分钟;(3)制作:在模具底部放置钢丝网片,把搅拌好的混凝土投进模具,用平板振动器振动整理,把混凝土的水泥浆振动出来,加上苯板、岩棉、珍珠岩等保温材料,然后在保温材料上面放置钢丝网片,加混凝土,继续用平板振动器振动,整理平整;( ...
【技术保护点】
一种轻质混凝土外墙板,其特征是其组成成分为:粗陶粒(φ0.5‑1.0cm)、中陶粒(φ0.3‑0.5cm)、陶粒粉末(φ0.3cm以下)、水泥、防水剂、减水剂、防冻剂;其成分比例为(重量计):粗陶粒(φ0.5‑1.0cm)34.5‑43%、中陶粒(φ0.3‑0.5cm)6.9‑17.2%、陶粒粉末(φ0.3cm以下)13.8‑25.8%、水泥13‑21%、防水剂0.13‑0.92%、减水剂0.098‑0.69%、防冻剂0.065‑1.15%。
【技术特征摘要】
1.一种轻质混凝土外墙板,其特征是其组成成分为:粗陶粒(φ0.5-1.0cm)、中陶粒(φ0.3-0.5cm)、陶粒粉末(φ0.3cm以下)、水泥、防水剂、减水剂、防冻剂;其成分比例为(重量计):粗陶粒(φ0.5-1.0cm...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。