微米级二氧化锡的制备方法技术
Preparation of micron grade two tin oxide
The preparation method for providing a two micron tin oxide, which comprises the following steps: heating and melting metal tin after water quenching into Xihua, then the reaction kettle in the tin flower water, heating and stirring after adding concentrated nitric acid for reaction, after the reaction is finished by centrifugation, washing and drying to obtain Metastannic Acid powder; the stannate powder is crushed calcining furnace for the first time after calcination, grinding again, and placed in the calcining furnace second after calcination, two micron tin oxide. The preparation method for simple and efficient and low cost by the method can get two micron tin oxide powder with high purity, uniform size and morphology.
【技术实现步骤摘要】
微米级二氧化锡的制备方法
本申请涉及半导体材料领域，尤其涉及一种微米级二氧化锡的制备方法。
技术介绍
二氧化锡是一种宽禁带的n型半导体金属氧化物，主要有类球形和棱柱形两种形态，属于四方晶系。高纯度的二氧化锡为白色粉末，经过加热处理发生晶型转变可显紫红色。微米级的二氧化锡被广泛应用在导电玻璃、半导体、陶瓷、气体传感器以及电子元件上。以作为银锡触头材料的原料为例，微米级的二氧化锡除了尺度要求外，还需要尺寸分布均一、呈类球形、纯度高、耐破损、无焊合现象等。公开日为2014年3月12日的中国专利申请CN103626222A公开了采用试剂级的锡酸钠为原料，通过滴加碳酸铵溶液、碳酸氢铵溶液或者碳酸铵和碳酸氢铵的混合溶液，控制反应液的pH值范围在9.0～10.0之间，制备出高分散性的水合氢氧化锡；再通过强酸调整氢氧化锡的pH值，获得偏锡酸固体；最后将偏锡酸固体直接置于高温煅烧炉中进行脱水处理，得到微米级的二氧化锡粉体。但是该方法采用的原料锡酸钠纯度较低、价格较高，且获取二氧化锡的前躯体偏锡酸的工艺复杂，引入的其他杂质离子不仅会降低产品的纯度而且会增加洗涤的难度。公开日为2005...
【技术保护点】
一种微米级二氧化锡的制备方法，其特征在于，包括步骤：S1，将金属锡加热熔化后水淬成锡花，然后将锡花置于含水的反应釜内，升温后加入浓硝酸并搅拌进行反应，反应结束后经离心、洗涤、干燥得到偏锡酸粉体；S2，将偏锡酸粉体粉碎后置于煅烧炉内进行第一次煅烧，之后再次粉碎，并置于煅烧炉内进行第二次煅烧，结束后得到微米级二氧化锡。
【技术特征摘要】
1.一种微米级二氧化锡的制备方法，其特征在于，包括步骤：S1，将金属锡加热熔化后水淬成锡花，然后将锡花置于含水的反应釜内，升温后加入浓硝酸并搅拌进行反应，反应结束后经离心、洗涤、干燥得到偏锡酸粉体；S2，将偏锡酸粉体粉碎后置于煅烧炉内进行第一次煅烧，之后再次粉碎，并置于煅烧炉内进行第二次煅烧，结束后得到微米级二氧化锡。2.根据权利要求1所述的微米级二氧化锡的制备方法，其特征在于，步骤S1中，升温至50℃～100℃后加入浓硝酸进行反应，反应时间为24h～34h。3.根据权利要求1所述的微米级二氧化锡的制备方法，其特征在于，步骤S1中，浓硝酸的质量分数为68％±3％。4.根据权利要求1所述的微米级二氧化锡的制备方法，其特征在于，步骤S1中，浓硝酸的加入速率为15mL/h～25mL/h。5.根据权利要求1所述的微米级二...
【专利技术属性】
技术研发人员：王权，朱刘，王艳，黄娟，刘佳，利镇升，
申请(专利权)人：清远先导材料有限公司，
类型：发明
国别省市：广东,44