The invention relates to a preparation method of a kind of two tin oxide nano material, the method comprises the following steps: using stannous chloride as the raw material, the measured after adding to quantitative volume ratio (1: 1) in the mixed solution of ethanol and deionized water, acrylic acid 0.5ml was added dropwise into the solution 10min, magnetic stirring, adding ammonia to adjust PH, magnetic stirring 10min, the solution set autoclave at 100 ~ 180 DEG C for 1 to 24 hours after cooling were washed with water and ethanol for several times, two meters of tin oxide is obtained after drying material. The invention has the advantages of simple process, good repeatability and batch production. At the same time, the two tin oxide microspheres prepared by the invention has a large specific surface area and excellent photocatalytic performance.
【技术实现步骤摘要】
本专利技术属于锡的氧化物的制备，涉及一种二氧化锡微球的制备方法。该方法利用水热法，通过控制反应物的量以及试验参数，得到了形貌和尺寸均一的二氧化锡微米球，该材料有望进一步应用于光催化反应。
技术介绍
二氧化锡是一种重要的宽带隙N型半导体材料，其禁带宽度Eg＝3.6eV(300K)，是一种重要的功能材料。而纳米尺度的二氧化锡材料因其具有特殊的光电特性和良好的机械、催化、光敏、气敏性能而受到极大的关注。在多个领域如陶瓷、颜料、磁记录材料、气敏元件、透明电极材料、储氢材料、催化材料、锂电池、太阳能电池等方面有着潜在的应用价值。到目前为止，采用不同的实验技术制备出了形貌各异的氧化锡纳米材料。如采用热蒸发法、激光剥离法、元素Sn的高温氧化法、微波法、等离子体法等技术制备出了二氧化锡纳米球、棒、管、线、带等。从制备工艺上来看，这些方法一般需要较高的温度、或是对仪器有着较高的要求。因此，寻找设备简单、产量高、成本低、产物性能稳定、无需二次处理的方法是现在合成技术所追求的目标。
技术实现思路
本专利技术所要解决的首要技术问题是提供一种工艺简单、成本低的二氧化锡微球的制备方法。本专利技...
【技术保护点】
一种二氧化锡微球的制备方法，其特征在于包括如下步骤：(1)称取适量水溶性的锡盐，加入溶剂为去离子水：乙醇为1∶1，使锡盐的浓度为0.2mol/L，磁力搅拌20min的A液；(2)再移取0.5～1ml丙烯酸，逐滴加入到A液中，磁力搅拌10min得B液；(3)缓慢滴加25％的氨水溶液，调至pH至5‑7，磁力搅拌20min得C液；(4)量取10～20ml C液放入到25～50ml反应釜中，保持温度在100～180℃，静置1～24h；(5)用蒸馏水和乙醇各洗涤三次，置于60℃烘箱中干燥6h；(6)将干燥后的产物置于马弗炉中，500℃条件下焙烧4h得到所要制备的纳米球状二氧化锡。
【技术特征摘要】
1.一种二氧化锡微球的制备方法，其特征在于包括如下步骤：(1)称取适量水溶性的锡盐，加入溶剂为去离子水：乙醇为1∶1，使锡盐的浓度为0.2mol/L，磁力搅拌20min的A液；(2)再移取0.5～1ml丙烯酸，逐滴加入到A液中，磁力搅拌10min得B液；(3)缓慢滴加25％的氨水溶液，调至pH至5-7，磁力搅拌20min得C液；(4)量取10～20mlC液放入到25～50ml反应釜中，保持温度在100～180℃，静置1～24...
【专利技术属性】
技术研发人员：储德清，王振凤，张永方，王立敏，王立鹏，
申请(专利权)人：天津工业大学，
类型：发明
国别省市：天津;12