The invention discloses a surface treatment process, particularly discloses a plastic surface treatment process, which comprises the following steps: A, the preparation of plastic parts; step two, the plastic pretreatment; step three, the pretreatment of plastic parts into a vacuum environment for coating; step four, plastic a coating after the anodic oxidation to form a conductive oxide layer and colored plastic parts get a desired color. The plastic film is coated by the plastic parts, then anodized and coloured to obtain the required color of the plastic parts, which solves the defects of metal parts such as metal and texture. The products are exquisite and beautiful, and have good metal texture. The heat dissipation and wear resistance are excellent.
【技术实现步骤摘要】
一种塑胶件表面处理工艺
：本专利技术涉及表面处理工艺，特别涉及了一种塑胶件表面处理工艺。
技术介绍
：塑胶材料具有易成型、质轻等优点，广泛应用于消费类电子、IT、家电等产品的结构件、壳体。随着消费者对产品外观的要求越来越高，部分中高端产品转而使用金属件如铝合金材料，但基于成本的考虑，为数众多的产品仍然采用塑胶的结构件及壳体。塑胶件的色彩虽然可以多种多样，但手感差，耐磨等性能差，无金属质感。塑胶件表面处理的常用方式是喷涂、烤漆，无法满足消费者对金属质感的期待。消费类电子、IT、家电等产品的结构件、壳体采用金属件(主要为铝及铝合金材料)制作时，因其大部分加工过程是用型材以CNC加工而成，工艺复杂、成本高昂，并且较为复杂的结构形状以CNC亦难于加工。
技术实现思路
：本专利技术的目的是提供一种塑胶件的表面处理工艺，以弥补现有技术之不足，直接在塑胶件表面进行镀膜，解决塑胶件产品表面无金属质感、耐磨性能差等缺陷，达到塑胶件的表面金属化效果，同时提高生产效率、降低成本，为实现以上目的，本专利技术的技术方案为：一种塑胶件表面处理工艺，包括：步骤一，制备塑胶件；步骤二，将塑胶件进行前...
【技术保护点】
一种塑胶件表面处理工艺，其特征在于：包括步骤一，制备塑胶件；步骤二，将塑胶件进行前处理；步骤三，将前处理后的塑胶件置入真空环境中进行镀膜；步骤四，将镀膜后的塑胶件进行阳极氧化以形成不导电的氧化层并着色得到所需颜色的塑胶件。
【技术特征摘要】
1.一种塑胶件表面处理工艺，其特征在于：包括步骤一，制备塑胶件；步骤二，将塑胶件进行前处理；步骤三，将前处理后的塑胶件置入真空环境中进行镀膜；步骤四，将镀膜后的塑胶件进行阳极氧化以形成不导电的氧化层并着色得到所需颜色的塑胶件。2.根据权利要求1所述的塑胶件表面处理工艺，其特征在于：所述塑胶件为耐300℃±100℃温度的材料。3.根据权利要求1所述的塑胶件表面处理工艺，其特征在于：所述真空环境的温度为100-300℃。4.根据权利要求1所述的塑胶件表面处理工艺，其特征在于：所述镀膜的时...