The invention discloses a low temperature impact resistant polypropylene composition, by weight, including 40 components: polypropylene resin 75, hydrogenated styrene butadiene block copolymer SEBS5 20; POE5 25 polyolefin elastomer. The invention of the low temperature impact resistant polypropylene composition by selecting specific weight content of hydrogenated styrene butadiene SEBS diblock copolymer and polyolefin elastomer POE as toughening agent, enhance the shock resistance performance of polypropylene composition especially low-temperature impact resistance performance, the resistance of the notched Charpy impact strength of prepared low temperature impact polypropylene composition by placing the sample 4H in the under 30 DEG C after more than 5 KJ/m
【技术实现步骤摘要】
一种耐低温冲击聚丙烯组合物
本专利技术涉及聚丙烯的改性，特别涉及到一种耐低温冲击聚丙烯组合物。
技术介绍
聚丙烯是汽车用塑料中用量最大的品种，具有密度低、性能好、易加工等特点，已成为车用塑料中用量最大的品种。然而聚丙烯耐低温冲击性能差，当汽车在寒冷天气下聚丙烯塑料会产生形变，影响行驶安全和汽车外观。为了提高聚丙烯的低温韧性，常添加弹性体进行增韧。公开号为CN103665570A采用氧化二异丙苯与聚烯烃弹性体交联得到XPOE作为增韧剂；CN103087429B采用己烯和辛烯为支链的多支链聚乙烯为裂纹扩散的抑制剂，提升聚丙烯材料的耐低温冲击性能，然而上述专利公开的聚丙烯组合物存在耐冲击性能不足的缺陷，特别是在温度较低的条件下耐冲击性能改善不明显，远达不到汽车在低温恶劣条件下安全行驶的需求。因此，如何开发出一种耐低温冲击聚丙烯组合物成为当今社会亟待解决的问题。
技术实现思路
本专利技术要解决的技术问题为提供一种耐低温冲击聚丙烯组合物，所述耐低温冲击聚丙烯组合物所制得的样品在-30℃条件下放置4h后的简支梁缺口冲击强度大于5.0KJ/m2。为了解决上述问题，采用以下技术方案：...
【技术保护点】
一种耐低温冲击聚丙烯组合物，其特征在于，按重量份计，包括以下组分：聚丙烯树脂 40‑75份氢化苯乙烯‑丁二烯嵌段共聚物SEBS 5‑20份聚烯烃弹性体POE 5‑25份。
【技术特征摘要】
1.一种耐低温冲击聚丙烯组合物，其特征在于，按重量份计，包括以下组分：聚丙烯树脂40-75份氢化苯乙烯-丁二烯嵌段共聚物SEBS5-20份聚烯烃弹性体POE5-25份。2.根据权利要求1所述的一种耐低温冲击聚丙烯组合物，其特征在于，所述氢化苯乙烯-丁二烯嵌段共聚物SEBS的单体单元中苯乙烯、乙烯和丁二烯的重量比例的范围为18-35：40-60：5-42。3.根据权利要求2所述的一种耐低温冲击聚丙烯组合物，其特征在于，所述氢化苯乙烯-丁二烯嵌段共聚物SEBS的单体单元中苯乙烯、乙烯和丁二烯的重量比例的范围为21-28：45-55：17-34。4.根据权利要求1所述的一种耐低温冲击聚丙烯组合物，其特征在于，所述聚烯烃弹性体POE的玻璃化转变温度为-52℃~-50℃。5.根据权利要求1所述的一种耐低温冲击聚丙烯组合物，其特征在于，所述POE的熔体质量流动速率以ISO1133标准，在190℃，2.16Kg条件下为0.3~2g/10min。6.根据权利要求1所述的一种耐低温冲击聚丙烯组合物，其特征在于，所述POE密度按照ISO180测试为0.85...