一种具有规则孔结构碳材料的制备方法技术

本发明专利技术公开了一种具有规则孔结构碳材料的制备方法，包括如下步骤：(1)室温下，将聚偏二卤乙烯、溶剂和脱卤剂进行球磨，并利用球磨过程中反应得到的气体来对固体物质进行鼓泡造孔，然后脱除溶剂；(2)在惰性气体保护下，缓慢升温，高温焙烧步骤(1)得到的产物即得到具有规则孔结构碳材料。本发明专利技术的制备方法时间短，不受反应物量的限制，具有直接量产的可行性。

A preparation method of carbon materials with regular pore structure

The invention discloses a preparation method with regular pore structure of carbon material, which comprises the following steps: (1) at room temperature, the two polyvinylidene vinyl halide, solvent and milling agent dehalogenation, and to the bubbling pore of solids by gas reaction ball milling process, and then removing the solvent slow; (2) under the protection of inert gas, heating, high temperature calcination steps (1) the product is obtained with regular pore structure of carbon materials. The preparation method of the invention has short time, is not limited by the amount of reactants, and has the feasibility of direct production.

【技术实现步骤摘要】
一种具有规则孔结构碳材料的制备方法
本专利技术属于材料的制备领域，具体涉及具有规则孔结构碳材料的制备方法。
技术介绍
规则孔结构碳材料具有广泛而重要的意义，特别是近些年来，面向能源领域的应用，规则孔结构碳材料作为载体材料，被开发得到一系列的高效高性能的规则孔结构碳，应用拓展至催化电化学反应、能量存储等热点领域。其制备方法主要为模板法，且集中使用氧化硅系球状(J.Am.Chem.Soc.2002,124,9382-9383/J.Am.Chem.Soc.2011,133,15148–15156)或柱状模板(J.Am.Chem.Soc.2006,128,11652-11662)法制备规则孔结构碳材料。该制备方法的优势在于：规则孔碳碳材料的孔径可以通过预设的硅氧体的尺寸进行调节，缺点在于：制备过程繁琐，耗时较长，如在J.Am.Chem.Soc.2006,128,11652-11662文献中提到，完成规则孔结构的碳材料的制备需要经历近40小时的时间。如何缩短制备时间，同时保障碳材料中孔道结构的规则排布，仍旧是材料合成领域的一大挑战。
技术实现思路
本专利技术提供了一种使用原位碳化产生的气体作为模板本文档来自技高网...

【技术保护点】
一种具有规则孔结构碳材料的制备方法，其特征在于，包括如下步骤：(1)室温下，将聚偏二卤乙烯、溶剂和脱卤剂进行球磨，并利用球磨过程中反应得到的气体来对固体物质进行鼓泡造孔，然后脱除溶剂；(2)在惰性气体保护下，缓慢升温，高温下焙烧步骤(1)得到的产物即得到具有规则孔结构碳材料。

【技术特征摘要】
1.一种具有规则孔结构碳材料的制备方法，其特征在于，包括如下步骤：(1)室温下，将聚偏二卤乙烯、溶剂和脱卤剂进行球磨，并利用球磨过程中反应得到的气体来对固体物质进行鼓泡造孔，然后脱除溶剂；(2)在惰性气体保护下，缓慢升温，高温下焙烧步骤(1)得到的产物即得到具有规则孔结构碳材料。2.根据权利要求1所述的具有规则孔结构碳材料的制备方法，其特征在于，所述室温为0～30℃；所述球磨的球磨机转速为10～50Hz，时间为0.1～10小时；所述脱除溶剂的温度为40～60℃。3.根据权利要求1所述的具有规则孔结构碳材料的制备方法，其特征在于，所述的聚...

【专利技术属性】
技术研发人员：孙晓明，张国新，韩标，王琳，
申请(专利权)人：北京化工大学，
类型：发明
国别省市：北京,11