一种环氧树脂胶膜及其制备方法技术
A kind of epoxy resin film and its preparation method
The present invention provides an epoxy resin film and a preparation method thereof. The method comprises the following steps: using two hydroxy propionic acid as monomer, pentaerythritol as core and toluene as solvent, catalyst A reaction, dehydration, removal of the solvent to obtain hydroxyl terminated hyperbranched polymer; adding hyperbranched polymer and epichlorohydrin in the reaction vessel, the ring opening reaction, catalyst B, occurrence of cyclization reaction to obtain hyperbranched epoxy resin; epoxy resin and hyperbranched epoxy resin mixture, adding curing agent, epoxy resin was prepared by hot melt adhesive film.
【技术实现步骤摘要】
一种环氧树脂胶膜及其制备方法
本专利技术涉及复合材料领域，更具体地，涉及一种环氧树脂胶膜及其制备方法。
技术介绍
随着飞机和风力发电等领域的功能化、集成化的要求不断提高，对应的封装材料的力学性能也提出了更高的要求。由于环氧树脂具有耐腐蚀性强、疲劳强度高、电绝缘性好等优良的机械性能，目前使用环氧树脂作为基体的复合材料越来越多，但是其冲击强度和弯曲强度等力学性能有待提高。通常需要加入增韧剂来提高其韧性和强度。超支化聚醚型环氧聚合物可以作为一种添加剂对双酚A型环氧树脂起到增韧增强的目的，但形成超支化聚醚型环氧聚合物时，需要氮气保护，不利于大规模生产，并且将超支化聚醚型环氧聚合物作为添加剂时，需要使用促进剂等，步骤相对较为繁琐，且最终产品的韧性和强度等力学性能均不佳，无法满足实际需求。
技术实现思路
本专利技术通过利用环氧氯丙烷间接法制备超支化环氧树脂，并且按照一定比例加入128环氧树脂，提高了环氧树脂胶膜的韧性和强度等力学性能。并且反应过程简单，不需要使用促进剂等，同时制备的超支化环氧树脂具有较强的增韧增强的效果。本专利技术通过优化环氧树脂的合成过程，以二羟基丙酸为单体、季...
【技术保护点】
一种制备环氧树脂胶膜的方法，其特征在于，包括：以二羟基丙酸为单体、季戊四醇为核、甲苯为溶剂，加入催化剂A，反应，去除溶剂得到端羟基超支化聚合物；在反应容器中加入所述端羟基超支化聚合物和环氧氯丙烷，发生开环反应，加入催化剂B，发生关环反应，得到超支化环氧树脂；将环氧树脂与所述超支化环氧树脂混合，加入固化剂，通过热熔法制备得到环氧树脂胶膜。
【技术特征摘要】
1.一种制备环氧树脂胶膜的方法，其特征在于，包括：以二羟基丙酸为单体、季戊四醇为核、甲苯为溶剂，加入催化剂A，反应，去除溶剂得到端羟基超支化聚合物；在反应容器中加入所述端羟基超支化聚合物和环氧氯丙烷，发生开环反应，加入催化剂B，发生关环反应，得到超支化环氧树脂；将环氧树脂与所述超支化环氧树脂混合，加入固化剂，通过热熔法制备得到环氧树脂胶膜。2.根据权利要求1所述的方法，其特征在于，所述二羟基丙酸和所述季戊四醇的物质的量比为4-60:1。3.根据权利要求1所述的方法，其特征在于，所述催化剂A为质量分数为2％的对甲苯磺酸或钛酸正丁酯。4.根据权利要求1所述的方法，其特征在于，所述反应的时间为10-14小时，所述反应的温度为110～130℃。5.根据权利要求1所述的方法，其特征在于，所述端羟基超支化聚合物和所述环氧氯丙烷的官能团比为1:5...
【专利技术属性】
技术研发人员：不公告发明人，
申请(专利权)人：洛阳尖端技术研究院，洛阳尖端装备技术有限公司，
类型：发明
国别省市：河南,41