The invention discloses a preparation method of integral resin sand mold, which is made by mixing the prepared quartz sand, furan resin and hardener in the corresponding proportion and pouring into the model for static molding, so as to be used for casting and producing fused zirconia corundum bricks. The beneficial effects of sand strong integrity, thus the size of small deformation, low manufacturing cost, good air permeability, easy casting sand in gas discharge, thus casting the electric size of fused zirconia corundum brick brick inside the body of small deformation, high density, low porosity, high rate of qualified products. Brick size and quality are better than water glass sand production; rough brick grinding parts are reduced, reduce processing costs, reduce product cost, improve economic efficiency, the preparation method has the advantages of simple operation, can be produced in large quantities.
【技术实现步骤摘要】
一种整体树脂砂型制备方法
本专利技术属于铸造
，具体涉及一种整体树脂砂型制备方法。
技术介绍
目前国内电熔锆刚玉砖生产厂家所用的砂型多为组合式的水玻璃砂型，使用此种砂型浇铸时，易造成砖体变形大、内部致密度不高等缺点，产品合格率低。此外，对浇铸成型合格的电熔锆刚玉砖为毛坯砖，还需进行研磨加工，待表面达到一定光洁度后，才能交付给客户，采用水玻璃砂型生产的毛坯砖材，由于外形尺寸变形大，需要加工的部位研磨加工量也大，增加了研磨加工费用，制造成本高。
技术实现思路
为了克服现有
存在的上述技术问题，本专利技术的目的在于，提供一种整体树脂砂型制备方法，使用此种砂型浇铸的砖体内部致密度高、气孔率低、变形小、产品合格率高、研磨加工量少、制造成本低。本专利技术提供的一种整体树脂砂型制备方法，包括以下步骤：（1）选料：石英砂96-96.4份，呋喃树脂3.3-3.5份，硬化剂0.3-0.5份，石英砂采用的是二氧化硅含量大于95.5%，粒度为50-80目的石英砂；（2）混合将石英砂、呋喃树脂和硬化剂按比例加入混合器中，搅拌，研磨均匀，备用；（3）成型：将备用的混合料倒入模型中，在...
【技术保护点】
一种整体树脂砂型制备方法，其特征在于：包括以下步骤：（1）选料：石英砂96‑96.4份，呋喃树脂3.3‑3.5份，硬化剂0.3‑0.5份，石英砂采用的是二氧化硅含量大于95.5%，粒度为50‑80目的石英砂；（2）混合：将石英砂、呋喃树脂和硬化剂按比例加入混合器中，搅拌，研磨均匀，备用；（3）成型：将备用的混合料倒入模型中，在常温下，静置成型，自然干燥，若在生产急用的情况下，还可借助微波烘干机将砂型烘干。
【技术特征摘要】
1.一种整体树脂砂型制备方法，其特征在于：包括以下步骤：（1）选料：石英砂96-96.4份，呋喃树脂3.3-3.5份，硬化剂0.3-0.5份，石英砂采用的是二氧化硅含量大于95.5%，粒度为50-80目的石...
【专利技术属性】
技术研发人员：李玉敏，
申请(专利权)人：青岛天地铸造有限公司，
类型：发明
国别省市：山东,37