一种水泵初级电机联轴器制造技术

一种水泵初级电机联轴器，所述联轴器由以下重量份的原料组成：氟0.05％‑0.09％，铈0.03％‑0.07％，铼0.01％‑0.03％，碳化硅0.03％‑0.05％，碳0.18％‑0.42％，锰0.12％‑0.24％，硅0.15％‑0.20％，磷0.02％‑0.06％，氮0.03％‑0.08％，余量为铁。本发明专利技术联轴器通过控制铁中的碳、锰、硅等元素含量，消除内部缩松缩孔缺陷，增加致密性，使钢强度增加；耐磨层可以有效的减少联轴器与轴承之间的摩擦，延长联轴器使用寿命。

A primary motor coupling for water pump

A primary pump motor coupling, the coupling by weight of raw materials: 0.05% fluorine 0.09%, 0.03% CE 0.07%, rhenium 0.01% 0.03%, 0.03% 0.05% 0.18% silicon carbide, carbon 0.42%, Mn 0.12%, 0.24%, Si 0.15% 0.20%, P 0.02% 0.06%, 0.03% n 0.08%, margin iron. The coupling of the invention eliminates the shrinkage and shrinkage defects in the iron by controlling the contents of carbon, manganese and silicon in the iron, increasing the compactness and increasing the strength of the steel. The wearable layer can effectively reduce the friction between the shaft and the bearing and prolong the service life of the coupling.

【技术实现步骤摘要】
一种水泵初级电机联轴器
本专利技术涉及水泵
，具体涉及一种水泵初级电机联轴器。
技术介绍
联轴器的材料主要采用碳素钢和合金钢，联轴器毛坯一般采用碾压件和锻件，很少采用铸件，由于碳素钢比合金钢成本低，且对于应力集中的敏感性较小，所以得到广泛的应用。常用的碳素钢有30、40、50钢等，其中最常用的为45钢，为保证联轴器材料的机械性能，应对联轴器材料进行调质或正火处理。联轴器受载荷较小或用于不重要的场合时，可用普通碳素钢(如Q235A、Q275等)作为转轴的材料。但是当遇到载荷较大或者作为关键零部件时需要更高强度的碳素钢，同时作为电机使用的联轴器在高速转动时会产生大量的热量和机械磨损，热量需要通过联轴器进行散热，机械磨损一方面通过润滑油减少磨损，另一方面需要通过提高联轴器自身的强度减少磨损。
技术实现思路
本专利技术为解决上述问题，提供一种内部致密、强度高适用于水泵初级电机的联轴器。本专利技术所要解决的技术问题采用以下的技术方案来实现：一种水泵初级电机联轴器，所述联轴器由以下重量份的原料组成：氟0.05％-0.09％，铈0.03％-0.07％，铼0.01％-0.03％，碳化硅0.03％-本文档来自技高网...

【技术保护点】
一种水泵初级电机联轴器，其特征在于，所述联轴器由以下重量份的原料组成：氟0.05％‑0.09％，铈0.03％‑0.07％，铼0.01％‑0.03％，碳化硅0.03％‑0.05％，碳0.18％‑0.42％，锰0.12％‑0.24％，硅0.15％‑0.20％，磷0.02％‑0.06％，氮0.03％‑0.08％，余量为铁。

【技术特征摘要】
1.一种水泵初级电机联轴器，其特征在于，所述联轴器由以下重量份的原料组成：氟0.05％-0.09％，铈0.03％-0.07％，铼0.01％-0.03％，碳化硅0.03％-0.05％，碳0.18％-0.42％，锰0.12％-0.24％，硅0.15％-0.20％，磷0.02％-0.06％，氮0.03％-0.08％，余量为铁。2.如权利要求1所述的一种水泵初级电机联轴器，其特征在于，所述联轴器转轴表面附着有导热层。3.如权利要求2所述的一种水泵初级电机联轴器，其特征在于，所述导热层为单层或双层石墨烯。4.如权利要求3所述的一种水泵初级电机联轴器，其特征...

【专利技术属性】
技术研发人员：刘兴满，
申请(专利权)人：刘兴满，
类型：发明
国别省市：江苏,32