The invention discloses a chlorinated polyether modified material and preparation method thereof, which comprises the following parts by weight of raw material preparation: 6 nano glass fiber, 15 copies of 10 copies of the 5 modifier, 20 30 phr chloroprene rubber, 60 70 copies, 1 coupling chlorinated polyether the 0.3 agent, 3 copies of 0.6 copies of the crosslinking agent; the invention will pass for nano glass fiber and chlorinated polyether modification of glass fiber composite, and the nano dispersed in chlorinated polyether system, the modified high tensile strength material with excellent performance, is conducive to the application of chlorinated polyether in more in the field of.
【技术实现步骤摘要】
一种氯化聚醚改性材料及其制备方法
本专利技术涉及改性材料领域，具体涉及一种氯化聚醚改性材料及其制备方法。
技术介绍
氯化聚醚化学名称为聚3,3'-双(氯甲基)丁氧环，是由3,3'-双(氯甲基)丁氧环单体在催化剂存在下开环聚合制得。氯化聚醚具有较高的耐热性，耐化学腐蚀性和耐磨性，且吸水性小，机械性能高，其制品广泛应用于机械、电子，化工、医疗器械、日用器具、办公用具等方面。随着人们对材料拉伸性能要求的不断提高，未经拉伸增强改性的氯化聚醚已难以满足需求，因而，对氯化聚醚进行拉伸增强改性成为必要。现今对氯化聚醚的拉伸增强改性处理方法种类繁多，改性效果也很好，尤其是随着纳米材料的出现和应用，氯化聚醚的拉伸强度增加效果显著，使氯化聚醚能在更多领域大量使用，但也存在不足。纳米材料虽然具有拉伸强度增强效果好，添加量小的优点，但也存在分散困难，成本高等缺陷。在进行拉伸强度改性过程中，纳米材料分散不均会影响其拉伸增强效果，得到的改性材料拉伸强度偏低，对改性材料的生产和应用造成不利影响。
技术实现思路
本专利技术的目的在于克服现有改性材料拉伸强度较差的缺陷，提供一种氯化聚醚改性材料及其制备...
【技术保护点】
一种氯化聚醚改性材料，其特征在于，包括以下重量份原材料制备得到：6‑15份的纳米玻璃纤维、5‑10份的改性剂、20‑30份的氯丁橡胶、60‑70份的氯化聚醚、1‑3份的偶联剂、0.3‑0.6份的交联剂；所述改性剂为四氢呋喃与环氧氯丙烷组成的混合物；所述偶联剂为乙氧基硅烷偶联剂，所述交联剂为间氯过氧苯甲酸；所述氯丁橡胶的聚合度为200‑300；所述氯化聚醚聚合度为800‑1600。
【技术特征摘要】
1.一种氯化聚醚改性材料，其特征在于，包括以下重量份原材料制备得到：6-15份的纳米玻璃纤维、5-10份的改性剂、20-30份的氯丁橡胶、60-70份的氯化聚醚、1-3份的偶联剂、0.3-0.6份的交联剂；所述改性剂为四氢呋喃与环氧氯丙烷组成的混合物；所述偶联剂为乙氧基硅烷偶联剂，所述交联剂为间氯过氧苯甲酸；所述氯丁橡胶的聚合度为200-300；所述氯化聚醚聚合度为800-1600。2.根据权利要求1所述的改性材料，其特征在于，所述改性剂中四氢呋喃与环氧氯丙烷的物质的量之比为1︰1。3.根据权利要求1所述的改性材料，其特征在于，所述氯丁橡胶的聚合度为240-280。4.根据权利要求3所述的改性材料，其特征在于，所述氯丁橡胶的聚合度为260。5.根据权利要求1所述的改性材料，其特征在于，所述氯化聚醚聚...
【专利技术属性】
技术研发人员：舒春柳，
申请(专利权)人：四川力智久创知识产权运营有限公司，
类型：发明
国别省市：四川,51