A kind of breathable sound insulation foam plastic for packaging and its production method, which belong to the technical field of foamed plastic packaging box. Includes the following parts by weight were prepared polyether 40 60, three glycerol acetate 15 26 copies, 8 copies, 3 polyisobutylene sepiolite powder 10 25 vinyl, three (beta methoxyethoxy) 10 silane 15, lauryl alcohol polyoxyethylene 3 ether 5 copies, 12 copies, 8 cocopeat initiator 15 35 copies, 40 copies of the 20 foaming agent and inorganic insulation materials 5 15 copies, 5 copies of 1 crosslinking agent. Compared with the existing foam plastics used for electrical packaging, the invention has many excellent properties: light weight, high strength, absorbable impact load performance, heat insulation, sound insulation performance and breathability, and can be widely applied in industry, agriculture, architecture, transportation and other fields.
【技术实现步骤摘要】
一种包装用透气型隔音泡沫塑料及其生产方法
本专利技术涉及一种包装用透气型隔音泡沫塑料及其生产方法，属于泡沫塑料包装盒
技术介绍
泡沫塑料是由大量气体微孔分散于固体塑料中而形成的一类高分子材料，具有质轻、隔热、吸音、减震等特性，且介电性能优于基体树脂，用途很广；几乎各种塑料均可作成泡沫塑料，发泡成型已成为塑料加工中一个重要领域。泡沫塑料整体布满无数互相连通或互不连通的微孔而使表观密度明显降低的塑料，具有质轻、绝热、吸音、防震、耐潮、耐腐蚀等优点。泡沫塑料是以塑料为基本组分并含有大量气泡的聚合物材料,因此也可以说是以气体为填料的复合塑料。目前市场上用于电器产品包装的泡沫塑料存在硬度高、柔软性较差、质重、绝热效果差、透气效果不佳、抗震性能欠缺、耐腐蚀效果不佳等缺陷。
技术实现思路
本专利技术的目的是针对上述现有技术的不足，提供一种包装用透气型隔音泡沫塑料及其生产方法。本专利技术的技术方案如下：一种包装用透气型隔音泡沫塑料，其特征是，包括以下重量份的各组份制备而成：聚醚多元醇40-60份、甘油三醋酸酯15-26份、聚异丁烯3-8份、海泡石粉10-25份、乙烯基三(β...
【技术保护点】
一种包装用透气型隔音泡沫塑料，其特征是，包括以下重量份的各组份制备而成：聚醚多元醇40‑60份、甘油三醋酸酯15‑26份、聚异丁烯3‑8份、海泡石粉10‑25份、乙烯基三(β‑ 甲氧基乙氧基) 硅烷10‑15份、月桂醇聚氧乙烯醚3‑5份、椰糠8‑12份、引发剂15‑35份、发泡剂20‑40份、无机隔音材料5‑15份、交联剂1‑5份。
【技术特征摘要】
1.一种包装用透气型隔音泡沫塑料，其特征是，包括以下重量份的各组份制备而成：聚醚多元醇40-60份、甘油三醋酸酯15-26份、聚异丁烯3-8份、海泡石粉10-25份、乙烯基三(β-甲氧基乙氧基)硅烷10-15份、月桂醇聚氧乙烯醚3-5份、椰糠8-12份、引发剂15-35份、发泡剂20-40份、无机隔音材料5-15份、交联剂1-5份。2.根据权利要求1所述的一种包装用透气型隔音泡沫塑料，其特征是，所述无机隔音材料为硫酸钡、铅粉、铁粉、硅藻土的混合物。3.根据权利要求2所述的一种包装用透气型隔音泡沫塑料，其特征是，所述无机隔音材料中，硫酸钡、铅粉、铁粉、硅藻土的重...