The present invention provides a hydrophilic TC ceramic floor paint, which is characterized by weight, including composite inorganic material, 10~20; polyfunctional organic film-forming material, 5~10; titanium dioxide 1~2; dispersant 0.6 ~ 1; pigment 3; coupling agent 2; among them, many functional groups of organic functional groups in the membrane, the hydroxyl group accounted for 70% ~ 90%. The invention is composed of inorganic compound and multi functional organic film, which is introduced into a variety of hydroxyl groups to break through the incompatible difficulties of oil and water. Because of the high crosslinking density after curing, the hardness is very high, and the paint film is full and Hikaruzawa Ryorei. It can be comparable with high temperature sintered tiles, and has excellent penetration resistance.
【技术实现步骤摘要】
亲水型TC陶瓷地坪漆
本专利技术涉及一种亲水型TC陶瓷地坪漆,属于地坪漆领域。
技术介绍
地坪漆最早是由德国于1934年专利技术,主要是由油料、树料、颜色、溶剂等制成,主要分为装饰性地坪漆、重防腐地坪漆、耐重载地坪漆等。地坪漆由多种不同物质经混合、溶解、分散等许多道生产工艺制造而组成。地坪漆具有亮丽、真实、美观、耐磨、防水、防腐等特点。传统的环氧树脂地坪漆的缺点是:1、抗紫外线能力差;2、易刮伤和擦刮伤;3、环氧树脂地坪漆怕地下潮气;4、耐高温性能差。
技术实现思路
本专利技术的目的在于提供一种亲水型TC陶瓷地坪漆,以解决上述问题。本专利技术采用了如下技术方案:本专利技术提供一种亲水型TC陶瓷地坪漆,其特征在于,按重量份计,包括:复合无机物,10~20份;多官能团有机成膜物,5~10份;钛白粉1~2份;分散剂0.6~1份;颜料3份;偶联剂2份;其中,多官能团有机成膜物中的官能团,羟基基团所占比例为70%~90%。进一步,本专利技术的亲水型TC陶瓷地坪漆,还可以具有这样的特征:其中,复合无机物中含有高岭土5份。进一步,本专利技术的亲水型TC陶瓷地坪漆,还可以具有这样的特征:其中,复合无机物中含有硅酸锌5份。进一步,本专利技术的亲水型TC陶瓷地坪漆,还可以具有这样的特征:其中,多官能度有机成膜物中,含有丙烯酸树脂3份。进一步,本专利技术的亲水型TC陶瓷地坪漆,还可以具有这样的特征:其中,多官能团有机成膜物中,含有有机硅1份。专利技术的有益效果本专利技术的亲水型TC陶瓷地坪漆的综合性能远远优于常规地坪涂料,市场上的常规环氧地坪漆的硬度一般都不会超过4H铅笔硬度,且硬 ...
【技术保护点】
一种亲水型TC陶瓷地坪漆,其特征在于,按重量份计,包括:复合无机物,10~20份;多官能团有机成膜物,5~10份;钛白粉1~2份;分散剂0.6~1份;颜料3份;偶联剂2份;其中,所述多官能团有机成膜物中的官能团,羟基基团所占比例为70%~90%。
【技术特征摘要】
1.一种亲水型TC陶瓷地坪漆,其特征在于,按重量份计,包括:复合无机物,10~20份;多官能团有机成膜物,5~10份;钛白粉1~2份;分散剂0.6~1份;颜料3份;偶联剂2份;其中,所述多官能团有机成膜物中的官能团,羟基基团所占比例为70%~90%。2.如权利要求1所述的亲水型TC陶瓷地坪漆,其特征在于:其中,所述复合无机...
【专利技术属性】
技术研发人员:李学全,洪跃忠,张华,
申请(专利权)人:上海香榭丽涂料有限公司,
类型:发明
国别省市:上海,31