一种非晶态合金催化剂、其制备方法及其用于肼分解制氢的应用技术

本发明专利技术公开了一种非晶态合金催化剂，所述催化剂的组成通式为NixMyPz，其中Ni含量为45～80wt％，P含量为10～45wt％；M为金属添加剂，含量为0～10wt％。本发明专利技术还公开了所述非晶态合金催化剂的制备方法及其用于催化肼分解制氢中的用途。本发明专利技术地方非晶态合金催化剂用于分解肼制氢具有较高的催化活性、选择性高、易于回收与分离，并且不用添加其他助剂。

An amorphous alloy catalyst, its preparation method and its application to hydrogen production by hydrazine decomposition

The invention discloses an amorphous alloy catalyst. The composition of the catalyst is NixMyPz, where Ni content is 45 to 80wt%, P content is 10 ~ 45wt%, M is metal additive, and its content is 0 ~ 10wt%. The invention also discloses the preparation method of the amorphous alloy catalyst and the use of the catalyst for the catalytic decomposition of hydrazine. The local amorphous alloy catalyst has high catalytic activity, high selectivity, easy recovery and separation for the decomposition of hydrazine, and does not need to add other auxiliaries.

【技术实现步骤摘要】
一种非晶态合金催化剂、其制备方法及其用于肼分解制氢的应用
本专利技术属于催化剂领域，具体涉及一种非晶态合金催化剂、其制备方法及其用于肼分解制氢的应用。
技术介绍
氢作为一种能量密度达120kJ/g的清洁能源受到了高度关注。氢燃料电池作为利用氢能的主要方式，在应用上仍然面对着许多问题，其中最主要的问题就是如何快速高效的产氢以及如何高效安全的储氢。利用高压储罐进行物理储氢的方法，储氢量低且不便于携带，无法进行实际应用。化学储氢分为金属固体储氢及液态化合物储氢。其中固体材料存在着放氢速度慢、合成条件苛刻、连续使用时材料发生变质等问题，在氢燃料电池中，装载卸载困难的问题尤为突出，不适用于实际应用。因此液态储氢化合物是最为合适的移动设备上的储氢材料。液态储氢化合物包括环甲酸、甲醇、环烷烃、含B和N的化合物(如，NH3BH3N2H4BH3)及肼等。其中甲酸的含氢量4.3wt％，未达到美国能源部(DOE)提出的移动设备储氢材料氢含量≥4.5wt％的标准。虽然甲醇的含氢量为12.5wt％，环烷烃的含氢量14.3wt％、含B和N的化合物也达到了标准，但它们仍存在其他问题，如目前没有合适的催化剂用于甲醇本文档来自技高网...

【技术保护点】
一种非晶态合金催化剂，其特征在于，所述催化剂的组成通式为NixMyPz，其中Ni含量为45～80wt％，P含量为10～45wt％；M为金属添加剂，含量为0～10wt％。

【技术特征摘要】
1.一种非晶态合金催化剂，其特征在于，所述催化剂的组成通式为NixMyPz，其中Ni含量为45～80wt％，P含量为10～45wt％；M为金属添加剂，含量为0～10wt％。2.根据权利要求1所述的非晶态合金催化剂，其特征在于，所述M为Al、Fe、Co、Cu、Mo、Mn、Au、Ag、Pt、Pd、Rh、Ru、Ir、La中的一种或几种。3.一种根据权利要求1所述的非晶态合金催化剂的制备方法，其特征在于，包括以下步骤：(1)将熔融的Ni倒入P中，冷却至室温；(2)将M金属屑加入到步骤(1)得到的物质中，在真空冶炼炉中冶炼，制得合金；(3)将步骤(2)制...

【专利技术属性】
技术研发人员：邹吉军，王雨桐，潘伦，张香文，王莅，
申请(专利权)人：天津大学，
类型：发明
国别省市：天津,12