The invention belongs to the field of metal materials, and specifically discloses a tensile strength 590MPa grade ferrite bainite dual phase steel with low yield strength, high tensile strength, high elongation and low production cost and a preparation method thereof. The tensile strength of 590MPa ferrite bainite dual phase steel, composed of chemical components in the following weight percentage: C 0.06% ~ 0.09%, Si 0.15%, Mn 1.45% ~ 1.60%, 0.030% ~ 0.040% Nb, P = 0.02%, S = 0.003%, Al 0.015% ~ 0.050%, allowance for the impurity Fe and inevitable. Through the reasonable composition design, at the same time with the process of hot rolling can be obtained, the existing strength of plastic 590MPa iron excellent and reaming performance of ferrite bainite dual phase high strength steel; because of not adding Mo, Cr, Ni, Cu, V and other precious metals, so the invention provides a dual phase steel production low cost.
【技术实现步骤摘要】
抗拉强度590MPa级铁素体贝氏体双相钢及其制备方法
本专利技术属于金属材料领域，具体涉及一种抗拉强度590MPa级铁素体贝氏体双相钢及其制备方法。
技术介绍
近年来随着工艺技术的进步及轧制设备的快速更新，材料升级换代速度也在加快。同时，能源危机加重、政策要求节能减排及汽车轻量化的要求不断加深，低成本的高强钢呼声越来越高。双相钢具有低屈服强度、高抗拉强度和优良塑性等特点，被受汽车行业青睐。一直以来，国内外双相钢的生产多采用添加Mo、Cr、Ni、Cu、V等贵重合金元素的方案，导致钢材成本增加。随着市场竞争越来越激烈，生产制备低成本高性能的双相刚已成为各企业追求的目标。专利申请号为201310464989.7的专利技术专利申请公开了一种抗拉强度590MPa级具有高扩孔性能的铁素体贝氏体钢及其生产方法，其化学成分百分比为：C：0.05～0.10％，Si：0.10～0.50％，Mn：0.80～1.50％，P：0.03～0.06％，S≤0.008％，Cr：0.20～0.60％，Nb：0.03～0.06％，Al：0.01～0.06％，余量为Fe及不可避免杂质。虽然该专利中的抗...
【技术保护点】
抗拉强度590MPa级铁素体贝氏体双相钢，其特征在于，由以下重量百分比的化学成分组成：C 0.06％～0.09％，Si≤0.15％，Mn 1.45％～1.60％，Nb 0.030％～0.040％，P≤0.02％，S≤0.003％，Al 0.015％～0.050％，余量为Fe和不可避免的杂质。
【技术特征摘要】
1.抗拉强度590MPa级铁素体贝氏体双相钢，其特征在于，由以下重量百分比的化学成分组成：C0.06％～0.09％，Si≤0.15％，Mn1.45％～1.60％，Nb0.030％～0.040％，P≤0.02％，S≤0.003％，Al0.015％～0.050％，余量为Fe和不可避免的杂质。2.抗拉强度590MPa级铁素体贝氏体双相钢的制备方法，其特征在于，用于制备权利要求1所述的抗拉强度590MPa级铁素体贝氏体双相钢；该制备方法包括以下工艺流程：铁水脱硫→转炉冶炼复合吹炼→脱氧、合金化→炉后...
【专利技术属性】
技术研发人员：肖尧，吴菊环，李正荣，熊雪刚，
申请(专利权)人：攀钢集团攀枝花钢铁研究院有限公司，
类型：发明
国别省市：四川,51