本发明专利技术属于催化剂领域，具体涉及一种烟气用耐磨催化剂，由以下重量份的原料制成：三氧化二铝8‑15份、五氧化二钒0.5‑3份、氯化镁0.1‑0.3份、仲钨酸铵0.2‑0.4份、五氧化二锑0.1‑0.3份、二氧化钛5‑10份、三氧化钨1‑5份、氧化铜0.1‑0.6份。本发明专利技术催化剂从分子水平上克服了对零价汞氧化效率受燃煤氯含量影响的问题，兼具优异的零价汞氧化性能和脱硝性能。

A kind of wear-resistant catalyst for flue gas

The invention belongs to the field of catalyst, in particular to wear a catalyst for flue gas, made from the following raw materials in weight portion: three two aluminum oxide 8 15 copies, five of two vanadium 0.5 3 copies, 0.3 copies, 0.1 magnesium chloride ammonium paratungstate 0.2 0.4, five two 0.1 0.3 antimony oxide two, 10, 5 titanium trioxide 1 5 copies, 0.6 copies of 0.1 copper oxide. The catalyst overcomes the problem that the oxidation efficiency of zero valent mercury is affected by the content of chlorine in the coal at the molecular level, and has excellent zero valent mercury oxidation and denitrification performance.

【技术实现步骤摘要】
一种烟气用耐磨催化剂
本专利技术属于烟气用耐磨催化剂
，具体涉及一种烟气用耐磨催化剂。
技术介绍
国内燃煤电厂氮氧化物(NOx)减排进入攻坚阶段，对脱硝技术提出新要求。经济新常态下，国内工业企业用电量显著下降，加之能源结构调整、部分地区提高电力外购比例等政策因素导致电力供应结构改革，中电联发布的《2016年度全国电力供需形势分析预测报告》中预测2016年全年火电设备利用小时将进一步降低至4000小时左右，这意味着燃煤机组低负荷、变负荷运行工况将进一步增多。在低负荷状态下，烟气温度较低，传统催化剂活性不高，氮氧化物脱除效果有限；并且此时烟气中SO3、H2O、NH3等容易形成液态硫酸氢铵(ABS)粘附在催化剂表面，导致催化剂表面活性位被覆盖，使脱硝效果变差。
技术实现思路
本专利技术针对现有技术不足之处而提供的一种烟气用耐磨催化剂。为实现上述目的，本专利技术解决其技术问题所采用的技术方案是：一种烟气用耐磨催化剂，由以下重量份的原料制成：三氧化二铝8-15份、五氧化二钒0.5-3份、氯化镁0.1-0.3份、仲钨酸铵0.2-0.4份、五氧化二锑0.1-0.3份、二氧化钛5-10份、三氧化钨本文档来自技高网...

【技术保护点】
一种烟气用耐磨催化剂，其特征在于，由以下重量份的原料制成：三氧化二铝8‑15份、五氧化二钒0.5‑3份、氯化镁0.1‑0.3份、仲钨酸铵0.2‑0.4份、五氧化二锑0.1‑0.3份、二氧化钛5‑10份、三氧化钨1‑5份、氧化铜0.1‑0.6份。

【技术特征摘要】
1.一种烟气用耐磨催化剂，其特征在于，由以下重量份的原料制成：三氧化二铝8-15份、五氧化二钒0.5-3份、氯化镁0.1-0.3份、仲钨酸铵0.2-0.4份、五氧化二锑0.1-0.3份、二氧化钛5-10份、三氧化钨1-5份、氧化铜0.1-0.6份。2.根据权利要求1所述烟气用耐磨催化剂，其特征在于，由以下重量份的原料制成：三氧化二铝...