陶瓷和塑料复合材料的制备方法以及电子设备的外壳技术
Preparation of ceramic and plastic composite materials and the shell of electronic equipment
The invention discloses a preparation method of a ceramic and plastic composite material and a shell of an electronic device. The preparation method comprises the following steps: roughening the ceramic substrate to form nano level coarsening surface, and injecting plastic material onto the nano level roughened surface to form composite material. The bonding force between the ceramic matrix and the plastic material is greatly enhanced because of the nanoscale coarsening surface on the surface of the ceramic matrix. In the fall, the plastic material is not easy to separate from the ceramic matrix. In addition, the waterproof property of the composite material is good.
【技术实现步骤摘要】
陶瓷和塑料复合材料的制备方法以及电子设备的外壳
本专利技术涉及材料制备
，更具体地，涉及一种陶瓷和塑料复合材料的制备方法以及电子设备的外壳。
技术介绍
随着陶瓷制备技术的快速发展和人们审美的要求，越来越多的生产商选择陶瓷材料制作电子产品的外壳。为了安装电子元件，用户需要在陶瓷外壳的内壁上进行加工，例如打孔等。由于陶瓷本身的韧性低、强度高，故这些加工会导致陶瓷外壳损坏、破裂，导致陶瓷外壳的良品率降低。于是，人们在陶瓷外壳的内壁上复合塑料层，以便于进行加工。现有的陶瓷外壳和塑料复合体通常采用粘合剂粘结、卡扣卡合等方法制作。然而，这些方法得到的陶瓷外壳和塑料复合体的结合强度过低,无法通过电子产品的跌落测试以及防水测试。
技术实现思路
本专利技术的一个目的是提供一种陶瓷和塑料复合材料的制备方法的新技术方案。根据本专利技术的第一方面，提供了一种陶瓷和塑料复合材料的制备方法。该制备方法包括以下步骤：对陶瓷基体进行粗化处理，以形成纳米级粗化表面；将塑料材料注塑到所述纳米级粗化表面上，以形成复合材料。可选地，所述陶瓷基体选自氧化锆陶瓷、氧化铝陶瓷、氧化硅陶瓷、氧化钛陶瓷、氧化镁...
【技术保护点】
一种陶瓷和塑料复合材料的制备方法，其中，包括以下步骤：对陶瓷基体进行粗化处理，以形成纳米级粗化表面；将塑料材料注塑到所述纳米级粗化表面上，以形成复合材料。
【技术特征摘要】
1.一种陶瓷和塑料复合材料的制备方法，其中，包括以下步骤：对陶瓷基体进行粗化处理，以形成纳米级粗化表面；将塑料材料注塑到所述纳米级粗化表面上，以形成复合材料。2.根据权利要求1所述的陶瓷和塑料复合材料的制备方法，其中，所述陶瓷基体选自氧化锆陶瓷、氧化铝陶瓷、氧化硅陶瓷、氧化钛陶瓷、氧化镁陶瓷、氧化钙陶瓷、氮化硅陶瓷、氮化硼陶瓷和碳化硅陶瓷中的一种或者多种复合陶瓷。3.根据权利要求1所述的陶瓷和塑料复合材料的制备方法，其中，所述纳米级粗化表面的粗糙度为5-800nm。4.根据权利要求1所述的陶瓷和塑料复合材料的制备方法，其中，采用酸性溶液腐蚀的方法对所述陶瓷基体进行粗化处理，以形成所述粗化表面。5.根据权利要求4所述的陶瓷和塑料复合材料的制备方法，其中，所述酸性溶液的酸选自硫酸、氢氟酸、盐酸、磷酸和草酸中的至少一种。6.根据权利要求5所述的陶瓷和塑料复合材料的制备方法，其中，所述酸性溶液中酸的浓度大于或等于5g/L，酸性溶液的温度为10-120℃...
【专利技术属性】
技术研发人员：王成，刘利强，俞胜平，张法亮，
申请(专利权)人：歌尔股份有限公司，
类型：发明
国别省市：山东,37