The invention discloses a water-based environmental protection coating mold, the mold with water-based environmentally friendly coatings including dry and water to dry the dry mass of 100%, including 40% ~ 45% silica powder, zirconium silicate rock powder containing 35% ~ 30%, 15% ~ 20% graphite powder and binder of 0.8% ~ 1.2%. 1% ~ 1.5% lithium bentonite, 0.5% to 1% of the defoamer, bump powder 3% ~ 2.5%, 5% ~ 10% of the sintering agent. The mold is coated on the mold surface with water based environmental protection coating. It can effectively prevent holes, cracks, and retention marks, and the price is cheap, and it is safe and environmental.
【技术实现步骤摘要】
铸型用水基环保涂料
本专利技术涉及铸造涂料
，具体地，涉及一种铸型用水基环保涂料。
技术介绍
为了减少铸铁件生产过程中容易发生的孔洞、裂纹、留痕等问题提高铸铁件的表面质量，提高铸铁件落砂和清整效率和铸铁件的成品率，我们需要选用合适的铸型用涂料。而对于国产铸型用涂料存在以下几个问：涂料的消泡效果差，国产涂料在使用时，都会有或多或少的气泡，要完全消除泡沫不是很容易；涂料的流平性不佳，铸型浸涂后，表面有明显的留痕、堆积，上下涂层厚度不均匀；涂料与铸型的润湿性差。目前水基涂料国外涂料质量好，但是价格昂贵，国产涂料也有比较好的，涂料质量却不稳定，或多或少存在一些问题，整体质量与国外涂料差距比较大。针对上述问题，自主研发一种新型铸铁水基环保涂料就显得十分必要。
技术实现思路
本专利技术的目的是提供一种铸型用水基环保涂料，该铸型用水基环保涂料涂覆于铸型表面，可以有效地防止孔洞、裂纹、留痕现象产生，且价钱廉价，安全环保。为了实现上述目的，本专利技术提供了一种铸型用水基环保涂料，所述铸型用水基环保涂料包括干料和水，以干料的质量为100％计，干料包括40％～45％的硅砂粉，30％～...
【技术保护点】
一种铸型用水基环保涂料，其特征在于，所述铸型用水基环保涂料包括干料和水，以干料的质量为100％计，干料包括40％～45％的硅砂粉，30％～35％的含锆硅酸岩粉，15％～20％的石墨粉，0.8％～1.2％的结合剂，1.0％～1.5％的锂基膨润土，0.5％～1.0％的消泡剂，2.5％～3.0％的凹凸石粉，5％～10％的助烧结剂。
【技术特征摘要】
1.一种铸型用水基环保涂料，其特征在于，所述铸型用水基环保涂料包括干料和水，以干料的质量为100％计，干料包括40％～45％的硅砂粉，30％～35％的含锆硅酸岩粉，15％～20％的石墨粉，0.8％～1.2％的结合剂，1.0％～1.5％的锂基膨润土，0.5％～1.0％的消泡剂，2.5％～3.0％的凹凸石粉，5％～10％的助烧结剂。2.根据权利要求1所述的铸型用水基环保涂料，其中，所述铸型用水基环保涂料包括干料和水，以干料的质量为100％计，干料包括42％～44％的硅砂粉，32％～34％的含锆硅酸岩粉，16％～18％的石墨粉，0.8％～1.2％的结合剂，1.2％～1.5％的锂基膨润土，0.8％～1.0％的消泡剂，2.8％～3.0％的凹凸石粉，8％～10％的助烧结剂。3.根据权利要求1或2所述的铸型用水基环保涂料，其中，相对于1重量份的干料，水的含量为1.5-2.8重量份。4.根据权利要求1-3任一项所述的铸型用水基环保涂料，其中，硅砂粉、锆硅酸岩粉、石墨粉、变性淀粉、膨润土和凹凸石粉的粒径...
【专利技术属性】
技术研发人员：柴知章，张月茹，
申请(专利权)人：安徽信息工程学院，
类型：发明
国别省市：安徽,34