铝合金压铸高效水基脱模剂制造技术

本发明专利技术涉及一种铝合金压铸高效水基脱模剂，其组分及质量百分含量为：改性有机聚硅氧烷：10－18％；蜂蜡：3－6％；氧化聚乙烯蜡：2－5％；Span80：1－2％；OP‑10：3－8％；杂多糖生物高聚物增稠剂：0.0－0.8％；2,6二叔甲基对甲酚：0.05－0.2％；杀菌防腐剂：0.1－0.2％；消泡剂：0.05－0.1％；水：余量。本发明专利技术水基乳液脱模剂稳定性较强，高温润湿温度320℃且成膜性较好，容易在金属表面形成一层具有一定强度的均匀润滑膜，有效润滑成分在高温下发气平稳且持续。经在复杂铝合金压铸件生产中试用，脱模效果良好，且铸件表面光洁。

High efficiency water base demoulding agent for aluminum alloy die casting

The invention relates to a Aluminum Alloy casting high efficient water-based release agent, the components and the mass content of modified organic polysiloxane: 10 - 18%; 3 - 6%; beeswax: oxidized polyethylene wax: 2 - 5%; Span80:1 2%; OP 10:3 8%; polysaccharide biopolymer thickening agent: 0 - 0.8%; 2,6 Di methyl p-cresol: 0.05 - 0.2%: 0.1 - 0.2%; preservatives; defoaming agent: 0.05 - 0.1%: Water Margin. The water-based emulsion release agent has strong stability, high temperature and 320 degree temperature and good film forming property. It is easy to form a uniform lubricating film with a certain intensity on the surface of the metal, and the effective lubricant component is stable and continuous at high temperature. The effect of the die casting is good and the surface of the casting is bright and clean in the production of the complex aluminum alloy die casting.

【技术实现步骤摘要】
铝合金压铸高效水基脱模剂
本专利技术属于脱模剂领域，涉及铝合金压铸，尤其是一种铝合金压铸高效水基脱模剂。
技术介绍
水基脱模剂因具有脱模性好、少污染、所得铸件少气孔且表面光洁、调节模温以提高模具寿命、有利于自动化操作等诸多优点，铝合金压铸生产中有着广泛应用。针对目前国产水基脱模剂普遍存在脱模效果及性能稳定性较差等问题，从脱模剂配方及制备工艺确定、脱模剂性能检测和实际生产试用等方面展开研究。
技术实现思路
本专利技术的目的在于克服现有技术的不足之处，提供一种稳定性强、成膜性好的铝合金压铸高效水基脱模剂。本专利技术解决技术问题所采用的技术方案是：一种铝合金压铸高效水基脱模剂，其组分及质量百分含量为：而且，所述的改性有机聚硅氧烷为烷基改性硅油。而且，所述的杂多糖生物高聚物增稠剂分子式：(C35H49O29)n。而且，所述的杀菌防腐剂为杀菌剂MBM。而且，所述的消泡剂为乳化硅油。而且，本脱模剂的乳化温度60℃，乳化搅拌速度2000r/min，乳化时间15min。本专利技术根据铝合金压铸工艺原理和水基乳液脱模剂所起的作用，选择将高温稳定性、剪切稳定性、室温储存稳定性、油相液滴粒径及其分布、高温润湿本文档来自技高网...

【技术保护点】
一种铝合金压铸高效水基脱模剂，其组分及质量百分含量为：

【技术特征摘要】
1.一种铝合金压铸高效水基脱模剂，其组分及质量百分含量为：2.根据权利要求1所述的脱模剂，其特征在于：所述的改性有机聚硅氧烷为烷基改性硅油。3.根据权利要求1所述的脱模剂，其特征在于：所述的杂多...

【专利技术属性】
技术研发人员：孙兰凤，
申请(专利权)人：天津市澳路浦润滑科技股份有限公司，
类型：发明
国别省市：天津,12