一种瓷盆底盘的配方组成比例

本发明专利技术涉及一种配方，特别是涉及瓷盆底盘的配方。本发明专利技术的配方由片状模塑料制成，所述的片状模塑料由树脂糊和玻璃纤维制成，其中树脂糊的重量百分比为65％‑85％，玻璃纤维的重量百分比为15％‑40％。本发明专利技术的配方不会挥发苯乙烯的瓷盆底盘配方，不会对人体产生危害，同样也不会对环境产生污染。该配方在生产过程中玻璃纤维也不会飞溅，不会影响人体健康。依照该配方生产的瓷盆底盘加强层光滑、坚固、强度高。

A formula for the chassis of a porcelain basin

The invention relates to a formula, in particular to a formula for the chassis of a porcelain basin. The formula of the invention consists of sheet molding plastic, sheet molding comprising a resin paste and glass fiber, wherein the weight percentage of resin paste for 65% 85% weight percent of glass fiber is 15% 40%. The formula of the porcelain basin chassis of the invention can not volatilize the styrene chassis formulation, does not harm the human body, nor does it pollute the environment. In the process of production, the glass fiber will not spatter, and it will not affect the health of the human body. The ceramic basin chassis, which is produced according to the formula, is smooth, solid and high in strength.

【技术实现步骤摘要】
一种瓷盆底盘的配方
本专利技术涉及一种配方，特别是涉及瓷盆底盘的配方。
技术介绍
现有的瓷盆底盘主要是亚克力底盘，主要是有亚克力材料、不饱和树脂及增强材料制成，而现在的瓷盆底盘配方在生产过程中玻璃纤维的飞溅会对环境造成污染，苯乙烯也会挥发，对人体产生害处，同时也污染环境，另外按照传统的配方进行瓷盆底盘的制作会使得产品的加强层毛躁，不光滑。
技术实现思路
本专利技术旨在解决上述问题而提供一种安全、环保的瓷盆底盘的配方。一种瓷盆底盘的配方，由片状模塑料制成，其特征在于：所述的片状模塑料由树脂糊和玻璃纤维制成，其中树脂糊的重量百分比为65％-85％，玻璃纤维的重量百分比为15％-40％。一种瓷盆底盘配方，其特征在于：所述的树脂糊的重量百分比为80％-85％，所述的玻璃纤维的重量百分比为15％-20％。具体实施方式实施例1一种瓷盆底盘的配方，由片状模塑料制成，其特征在于：所述的片状模塑料由树脂糊和玻璃纤维制成，其中树脂糊的重量百分比为65％-85％，玻璃纤维的重量百分比为15％-40％。实施例2一种瓷盆底盘配方，其特征在于：所述的树脂糊的重量百分比为80％-85％，所述的玻璃纤维的重量百分比为1本文档来自技高网...

【技术保护点】
一种瓷盆底盘的配方，由片状模塑料制成，其特征在于：所述的片状模塑料由树脂糊和玻璃纤维制成，其中树脂糊的重量百分比为65％‑85％，玻璃纤维的重量百分比为15％‑40％。

【技术特征摘要】
1.一种瓷盆底盘的配方，由片状模塑料制成，其特征在于：所述的片状模塑料由树脂糊和玻璃纤维制成，其中树脂糊的重量百分比为65％-85％，玻璃纤维的重量百分比为15％-40％。2.如权利要求1所述的一种瓷盆底盘配方，其...

【专利技术属性】
技术研发人员：王慧，
申请(专利权)人：如皋市东照服装有限公司，
类型：发明
国别省市：江苏,32